EN 10028-6 Grade P500Q quenched and tempered (+QT)
EN 10028-6 Grade P500Q quenched and tempered (+QT) introduction
Weldable fine grain structural steel for pressure vessel application in the quenched and tempered condition.
Application temperature: -20 to 20 °C
Equivalent material: ASTM A738 Grade E, ASTM A738 Grade D, IS P500Q, DIN 1.8873, DIN BEStE500TM, EN 1.8873
EN 10028-6 Grade P500Q quenched and tempered (+QT) general
| Property | Value | Comment |
|---|---|---|
| Density | Density of 7.8 g/cm³ | Typical for Steel |
EN 10028-6 Grade P500Q quenched and tempered (+QT) thermal
| Property | Value | Comment |
|---|---|---|
| Coefficient of thermal expansion | Coefficient of thermal expansion of 11.96 1/K | Predicted Value |
| Specific heat capacity | Specific heat capacity of 442.3 J/(kg·K) | Predicted Value |
| Thermal conductivity | Thermal conductivity of 36.19 W/(m·K) | Predicted Value |
EN 10028-6 Grade P500Q quenched and tempered (+QT) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Boron | Boron of 0.005 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Carbon | Carbon of 0.18 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Chromium | Chromium of 1 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Copper | Copper of 0.3 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Manganese | Manganese of 1.7 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Molybdenum | Molybdenum of 0.7 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Nickel | Nickel of 1.5 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Niobium | Niobium of 0.05 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Nitrogen | Nitrogen of 0.015 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Phosphorus | Phosphorus of 0.025 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Silicon | Silicon of 0.6 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Sulfur | Sulfur of 0.01 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| - | Sulfur of 0.015 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Titanium | Titanium of 0.05 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Vanadium | Vanadium of 0.08 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
| Zirconium | Zirconium of 0.15 % | quenched and tempered (+QT) | EN 10028-6 | Flat |
EN 10028-6 Grade P500Q quenched and tempered (+QT) electrical
| Property | Value | Comment |
|---|---|---|
| Electrical conductivity | Electrical conductivity of 5 S/m | Predicted Value |
| Electrical resistivity | Electrical resistivity of 36 Ω·m | Predicted Value |
EN 10028-6 Grade P500Q quenched and tempered (+QT) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | - | Elastic modulus of 190 - 210 GPa | - | - | - | Typical for Steel |
| Elongation | - | Elongation of 13.8 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 15.5 % | - | - | - | Predicted Value, A80 |
| - | - | Elongation of 17.1 % | - | - | - | Predicted Value, Transverse |
| - | - | Elongation of 18.9 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 20.4 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 22.5 % | - | - | - | Predicted Value, A50 |
| - | 20 °C | Elongation of 17 % | quenched and tempered (+QT) | EN 10028-6 | Flat | - |
| Poisson's ratio | - | Poisson's ratio of 0.3 [-] | - | - | - | Typical for Steel |
| Reduction of area | - | Reduction of area of 40.2 % | - | - | - | Predicted Value |
| - | - | Reduction of area of 44.0 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | - | Shear modulus of 80.1 GPa | - | - | - | Predicted Value |
| Shear strength | - | Shear strength of 591.6 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 540 - 770 MPa | quenched and tempered (+QT) | EN 10028-6 | Flat | - |
| - | 20 °C | Tensile strength of 540 - 720 MPa | quenched and tempered (+QT) | EN 10028-6 | Flat | - |
| - | 20 °C | Tensile strength of 590 - 770 MPa | quenched and tempered (+QT) | EN 10028-6 | Flat | - |
| - | 20 °C | Tensile strength of 590 - 720 MPa | quenched and tempered (+QT) | EN 10028-6 | Flat | - |
| Yield strength | - | Yield strength of 311 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 331.4 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 438.1 MPa | - | - | - | Predicted Value, Transverse |
| - | - | Yield strength of 446.3 MPa | - | - | - | Predicted Value, RP02 |
| - | - | Yield strength of 476.2 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 524.7 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 565.8 MPa | - | - | - | Predicted Value, RP002 |
| - | 20 °C | Yield strength of 440 MPa | quenched and tempered (+QT) | EN 10028-6 | Flat | - |
| - | 20 °C | Yield strength of 480 MPa | quenched and tempered (+QT) | EN 10028-6 | Flat | - |
| - | 20 °C | Yield strength of 500 MPa | quenched and tempered (+QT) | EN 10028-6 | Flat | - |