EN 10028-6 Grade P460QH quenched and tempered (+QT)
  • Home
  • Material
  • EN 10028-6 Grade P460QH quenched and tempered (+QT)

EN 10028-6 Grade P460QH quenched and tempered (+QT)

EN 10028-6 Grade P460QH quenched and tempered (+QT) introduction

High-temperature resistant weldable fine grain structural steel for pressure vessel application in the quenched and tempered condition.
Application temperature: -20 to 300 °C

Equivalent material: IS P460QH, DIN 1.8871, DIN BEStE420TM, EN 1.8871

EN 10028-6 Grade P460QH quenched and tempered (+QT) general

Property Value Comment
Density Density of 7.8 g/cm³ Typical for Steel

EN 10028-6 Grade P460QH quenched and tempered (+QT) thermal

Property Value Comment
Coefficient of thermal expansion Coefficient of thermal expansion of 11.95 1/K Predicted Value
Specific heat capacity Specific heat capacity of 449.2 J/(kg·K) Predicted Value
Thermal conductivity Thermal conductivity of 36.72 W/(m·K) Predicted Value

EN 10028-6 Grade P460QH quenched and tempered (+QT) chemical

Property Value Condition Related Standards Shape
Boron Boron of 0.005 % quenched and tempered (+QT) EN 10028-6 Flat
Carbon Carbon of 0.18 % quenched and tempered (+QT) EN 10028-6 Flat
Chromium Chromium of 0.3 % quenched and tempered (+QT) EN 10028-6 Flat
- Chromium of 0.5 % quenched and tempered (+QT) EN 10028-6 Flat
Copper Copper of 0.3 % quenched and tempered (+QT) EN 10028-6 Flat
Manganese Manganese of 1.7 % quenched and tempered (+QT) EN 10028-6 Flat
Molybdenum Molybdenum of 0.5 % quenched and tempered (+QT) EN 10028-6 Flat
Nickel Nickel of 1 % quenched and tempered (+QT) EN 10028-6 Flat
Niobium Niobium of 0.05 % quenched and tempered (+QT) EN 10028-6 Flat
Nitrogen Nitrogen of 0.015 % quenched and tempered (+QT) EN 10028-6 Flat
Phosphorus Phosphorus of 0.025 % quenched and tempered (+QT) EN 10028-6 Flat
Silicon Silicon of 0.5 % quenched and tempered (+QT) EN 10028-6 Flat
Sulfur Sulfur of 0.01 % quenched and tempered (+QT) EN 10028-6 Flat
- Sulfur of 0.015 % quenched and tempered (+QT) EN 10028-6 Flat
Titanium Titanium of 0.03 % quenched and tempered (+QT) EN 10028-6 Flat
Vanadium Vanadium of 0.08 % quenched and tempered (+QT) EN 10028-6 Flat
Zirconium Zirconium of 0.05 % quenched and tempered (+QT) EN 10028-6 Flat

EN 10028-6 Grade P460QH quenched and tempered (+QT) electrical

Property Value Comment
Electrical conductivity Electrical conductivity of 5 S/m Predicted Value
Electrical resistivity Electrical resistivity of 36 Ω·m Predicted Value

EN 10028-6 Grade P460QH quenched and tempered (+QT) mechanical

Property Temperature Value Condition Related Standards Shape Comment
Elastic modulus - Elastic modulus of 190 - 210 GPa - - - Typical for Steel
Elongation - Elongation of 14.1 % - - - Predicted Value, A200
- - Elongation of 15.7 % - - - Predicted Value, A80
- - Elongation of 19.0 % - - - Predicted Value, A80 Transverse
- - Elongation of 20.1 % - - - Predicted Value, Transverse
- - Elongation of 20.4 % - - - Predicted Value, A5
- - Elongation of 24.2 % - - - Predicted Value, A50
- 20 °C Elongation of 19 % quenched and tempered (+QT) EN 10028-6 Flat -
Poisson's ratio - Poisson's ratio of 0.3 [-] - - - Typical for Steel
Reduction of area - Reduction of area of 40.5 % - - - Predicted Value
- - Reduction of area of 44.0 % - - - Predicted Value, Transverse
Shear modulus - Shear modulus of 80.3 GPa - - - Predicted Value
Shear strength - Shear strength of 559.5 MPa - - - Predicted Value
Tensile strength 20 °C Tensile strength of 500 - 720 MPa quenched and tempered (+QT) EN 10028-6 Flat -
- 20 °C Tensile strength of 500 - 670 MPa quenched and tempered (+QT) EN 10028-6 Flat -
- 20 °C Tensile strength of 550 - 720 MPa quenched and tempered (+QT) EN 10028-6 Flat -
- 20 °C Tensile strength of 550 - 670 MPa quenched and tempered (+QT) EN 10028-6 Flat -
Yield strength - Yield strength of 259.9 MPa - - - Predicted Value, RP1
- - Yield strength of 323.3 MPa - - - Predicted Value, RP1 Transverse
- - Yield strength of 429.1 MPa - - - Predicted Value, Transverse
- - Yield strength of 475.1 MPa - - - Predicted Value, RP02 Transverse
- - Yield strength of 516.7 MPa - - - Predicted Value, RP05
- - Yield strength of 535.1 MPa - - - Predicted Value, RP002
- 20 °C Yield strength of 400 MPa quenched and tempered (+QT) EN 10028-6 Flat -
- 20 °C Yield strength of 440 MPa quenched and tempered (+QT) EN 10028-6 Flat -
- 20 °C Yield strength of 460 MPa quenched and tempered (+QT) EN 10028-6 Flat -
- 50 °C Yield strength of 385 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 50 °C Yield strength of 425 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 50 °C Yield strength of 445 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 100 °C Yield strength of 365 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 100 °C Yield strength of 405 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 100 °C Yield strength of 425 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 150 °C Yield strength of 345 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 150 °C Yield strength of 385 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 150 °C Yield strength of 405 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 200 °C Yield strength of 320 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 200 °C Yield strength of 360 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 200 °C Yield strength of 380 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 250 °C Yield strength of 300 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 250 °C Yield strength of 340 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 250 °C Yield strength of 360 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 300 °C Yield strength of 280 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 300 °C Yield strength of 320 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02
- 300 °C Yield strength of 340 MPa quenched and tempered (+QT) EN 10028-6 Flat RP02

Our stringent quality control measures ensure consistent and reliable steel products.