EN 10025 Grade S275JRC as-rolled condition (+AR)
EN 10025 Grade S275JRC as-rolled condition (+AR) introduction
S275JRC is used for folding, section cold forming and cold drawing grade. The steel is applicable for temperatures up to -20 °C. Compared to S235JRC is achievable a saving of material due to the by 40 MPa higher yield point. Max. product thickness amounts 20 mm for folding and 8 mm for cold roll forming grades.
Equivalent material: JIS SS400, DIN QSt44-2, DIN 1.0128, DIN St 44-2, DIN QSt 44-2, DIN S275JRC, AFNOR S275JRC, BS S275JRC, JIS E275A, EN 1.0128
EN 10025 Grade S275JRC as-rolled condition (+AR) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10025 Grade S275JRC as-rolled condition (+AR) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -20 - 0 °C |
- |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10025 Grade S275JRC as-rolled condition (+AR) chemical
| Property |
Value |
| Carbon |
Carbon of 0.21 % |
| Manganese |
Manganese of 1.5 % |
| Nitrogen |
Nitrogen of 9E-3 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Sulfur |
Sulfur of 0.045 % |
EN 10025 Grade S275JRC as-rolled condition (+AR) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10025 Grade S275JRC as-rolled condition (+AR) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10025 Grade S275JRC as-rolled condition (+AR) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 22 % |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 14 - 18 % |
- |
| Elongation A80, transverse |
20.0 °C |
Elongation A80, transverse of 12 - 16 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 20 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 410 - 580 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 265 - 275 MPa |
- |