EN 10025-5 Grade S355J2W normalized or normalized formed (+N)
  • Home
  • Material
  • EN 10025-5 Grade S355J2W normalized or normalized formed (+N)

EN 10025-5 Grade S355J2W normalized or normalized formed (+N)

EN 10025-5 Grade S355J2W normalized or normalized formed (+N) introduction

The weather resistant steel S355J2W with improved atmospheric corrosion resistance (by generation of an conversion coating) has a minimum yield strength of 355 N/mm². It is applicated for welded, screwed and riveted constructions, e.g. structural engineering, bridge building, tank construction, exhaust systems, vehicle construction, toolbuilding.
The grid rate have to considered in the dimensioning process. An conventional surface protection is recommend at polluted air and necessary at long-time water wetting, constant wetness or close to the sea. Unweathered areas with condensate generation have to be adequate ventilated.
Before welding the coating have to be removed in a distance of 10 - 20 mm from the welding edge.
With increasing thickness, strength and carbon equivalent the occurence of cold cracks in the welding zone is possible.
The recommendation of the EURONORM Information No. 2 (EN 1011-2) have to considered.

Equivalent material: GB Q355NH, GB L53550, IS S355WD, IS SMA490, ASTM A588 Grade A, ASTM A588 Grade B, ASTM A588 Grade C, ASTM A588 Grade D, ASTM A588 Grade K, ASTM A709 Grade 50W, ASTM A871 Grade 60, UNS K11430, UNS K12043, UNS K11538, EN S355J2G2W, DIN WTSt52-3, DIN 1.8963, EN 1.8963, DIN WTSt 52-3, DIN St 52-3, DIN S355J2W, DIN S355J2G1W, BS WR50C, JIS SMA490BW, JIS SMA400AW, JIS SMA400BW, JIS SMA400CW, JIS SMA570W, JIS SMA490AW, DIN 1.8965, EN 1.8965, DIN S355J2G2W, ASTM Type IV Grade II

EN 10025-5 Grade S355J2W normalized or normalized formed (+N) general

Property Value Comment
Density Density of 7.8 g/cm³ Typical for Steel

EN 10025-5 Grade S355J2W normalized or normalized formed (+N) thermal

Property Value Comment
Coefficient of thermal expansion Coefficient of thermal expansion of 12.02 1/K Predicted Value
Specific heat capacity Specific heat capacity of 455 J/(kg·K) Predicted Value
Thermal conductivity Thermal conductivity of 36.13 W/(m·K) Predicted Value

EN 10025-5 Grade S355J2W normalized or normalized formed (+N) chemical

Property Value Condition Related Standards Shape
Carbon Carbon of 0.16 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire
Chromium Chromium of 0.4 - 0.8 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire
Copper Copper of 0.25 - 0.55 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire
Manganese Manganese of 0.5 - 1.5 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire
Molybdenum Molybdenum of 0.3 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire
Nickel Nickel of 0.65 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire
Phosphorus Phosphorus of 0.03 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire
Silicon Silicon of 0.5 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire
Sulfur Sulfur of 0.03 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire
Zirconium Zirconium of 0.15 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire

EN 10025-5 Grade S355J2W normalized or normalized formed (+N) electrical

Property Value Comment
Electrical conductivity Electrical conductivity of 3 S/m Predicted Value
Electrical resistivity Electrical resistivity of 35 Ω·m Predicted Value

EN 10025-5 Grade S355J2W normalized or normalized formed (+N) mechanical

Property Temperature Value Condition Related Standards Shape Comment
Elastic modulus - Elastic modulus of 190 - 210 GPa - - - Typical for Steel
Elongation - Elongation of 17.6 % - - - Predicted Value, A200
- - Elongation of 21.8 % - - - Predicted Value, A5
- - Elongation of 23.7 % - - - Predicted Value, A50
- 20 °C Elongation of 14 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire A80 Transverse
- 20 °C Elongation of 15 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire A80 Transverse
- 20 °C Elongation of 16 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire A80 Transverse
- 20 °C Elongation of 16 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire A80
- 20 °C Elongation of 17 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire A80
- 20 °C Elongation of 18 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire A80
- 20 °C Elongation of 18 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Elongation of 18 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Elongation of 19 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Elongation of 20 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Elongation of 20 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Elongation of 21 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Elongation of 22 % normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
Hardness, Brinell - Hardness, Brinell of 234 [-] - - - Predicted Value, Transverse
Poisson's ratio - Poisson's ratio of 0.3 [-] - - - Typical for Steel
Reduction of area - Reduction of area of 45.3 % - - - Predicted Value, Transverse
- - Reduction of area of 52.2 % - - - Predicted Value
Shear modulus - Shear modulus of 80.2 GPa - - - Predicted Value
Shear strength - Shear strength of 539.7 MPa - - - Predicted Value
Tensile strength 20 °C Tensile strength of 450 - 680 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Tensile strength of 450 - 630 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Tensile strength of 450 - 600 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Tensile strength of 450 - 680 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 450 - 630 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 450 - 600 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 470 - 680 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Tensile strength of 470 - 630 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Tensile strength of 470 - 600 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Tensile strength of 470 - 680 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 470 - 630 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 470 - 600 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 510 - 680 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Tensile strength of 510 - 630 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Tensile strength of 510 - 600 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Tensile strength of 510 - 680 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 510 - 630 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 510 - 600 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
Yield strength - Yield strength of 260.9 MPa - - - Predicted Value, RP1
- - Yield strength of 286.6 MPa - - - Predicted Value, RP1 Transverse
- - Yield strength of 388.1 MPa - - - Predicted Value, RP02
- - Yield strength of 393.3 MPa - - - Predicted Value, RP05
- - Yield strength of 407.9 MPa - - - Predicted Value, RP02 Transverse
- - Yield strength of 468.6 MPa - - - Predicted Value, RP002
- 20 °C Yield strength of 295 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Yield strength of 295 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Yield strength of 315 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Yield strength of 315 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Yield strength of 325 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Yield strength of 325 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Yield strength of 335 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Yield strength of 335 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Yield strength of 345 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Yield strength of 345 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Yield strength of 355 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire Transverse
- 20 °C Yield strength of 355 MPa normalized or normalized formed (+N) EN 10025-5, EN 10155 Strip, Sheet, Flat, Rod, Wire -

Be at the forefront of industry advancements by incorporating our innovative steel solutions.

-- Our promise

Similar or equivalent steel materials

Get a quote

Post Categories