EN 10025-4 Grade S460ML thermomechanically rolled
  • Home
  • Material
  • EN 10025-4 Grade S460ML thermomechanically rolled

EN 10025-4 Grade S460ML thermomechanically rolled

EN 10025-4 Grade S460ML thermomechanically rolled introduction

S460ML is a weldable fine-grained steel with a min. yield point of 460 N/mm². The steel is applicated in thermo mechanical rolled condition for several types of welded constructions such as fixed and movable storage container, high-pressure pipes, bridge and load-bearing constructions.
Subsequent heating above 580°C for thermo mechanical rolled products causes reduction of the strength properties.
Application limit: at -50°C is warranted a notch impact energy of 27J (longitudinal test specimen).
The carbon equivalent (by arrangement) amounts to:
for nominal size: 16

Equivalent material: UNI FeE460KTTM, DIN TStE460TM, IS S460ME, IS E460ML, DIN BTStE460TM, DIN 1.8838, EN 1.8838, DIN BTStE 460 TM, DIN TStE 460 TM, DIN S460ML, UNI FeE460 KTTM

EN 10025-4 Grade S460ML thermomechanically rolled general

Property Value Comment
Density Density of 7.8 g/cm³ Typical for Steel

EN 10025-4 Grade S460ML thermomechanically rolled thermal

Property Value Comment
Coefficient of thermal expansion Coefficient of thermal expansion of 11.84 1/K Predicted Value
Specific heat capacity Specific heat capacity of 455.2 J/(kg·K) Predicted Value
Thermal conductivity Thermal conductivity of 37.88 W/(m·K) Predicted Value

EN 10025-4 Grade S460ML thermomechanically rolled chemical

Property Value Condition Related Standards Shape
Aluminium Aluminium of 0.02 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire
Carbon Carbon of 0.16 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire
Chromium Chromium of 0.3 % thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire
Copper Copper of 0.55 % thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire
Manganese Manganese of 1.7 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire
Molybdenum Molybdenum of 0.2 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire
Nickel Nickel of 0.45 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar
- Nickel of 0.8 % thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire
Niobium Niobium of 0.05 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire
Nitrogen Nitrogen of 0.025 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire
Phosphorus Phosphorus of 0.025 % thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire
- Phosphorus of 0.03 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar
Silicon Silicon of 0.6 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire
Sulfur Sulfur of 0.02 % thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire
- Sulfur of 0.025 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar
Titanium Titanium of 0.05 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire
Vanadium Vanadium of 0.12 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire

EN 10025-4 Grade S460ML thermomechanically rolled electrical

Property Value Comment
Electrical conductivity Electrical conductivity of 7 S/m Predicted Value
Electrical resistivity Electrical resistivity of 35 Ω·m Predicted Value

EN 10025-4 Grade S460ML thermomechanically rolled mechanical

Property Temperature Value Condition Related Standards Shape Comment
Elastic modulus - Elastic modulus of 190 - 210 GPa - - - Typical for Steel
Elongation - Elongation of 12.2 % - - - Predicted Value, A200
- - Elongation of 15.1 % - - - Predicted Value, A80
- - Elongation of 17.6 % - - - Predicted Value, Transverse
- - Elongation of 19.2 % - - - Predicted Value, A80 Transverse
- - Elongation of 20.2 % - - - Predicted Value, A5
- - Elongation of 22.6 % - - - Predicted Value, A50
- 20 °C Elongation of 17 % thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire -
Hardness, Brinell - Hardness, Brinell of 246 [-] - - - Predicted Value, Transverse
Poisson's ratio - Poisson's ratio of 0.3 [-] - - - Typical for Steel
Reduction of area - Reduction of area of 41.9 % - - - Predicted Value
- - Reduction of area of 44.6 % - - - Predicted Value, Transverse
Shear modulus - Shear modulus of 80.3 GPa - - - Predicted Value
Shear strength - Shear strength of 528.9 MPa - - - Predicted Value
Tensile strength 20 °C Tensile strength of 490 - 720 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 490 - 710 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 490 - 690 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 490 - 680 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 490 - 660 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 500 - 720 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 500 - 710 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 500 - 690 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 500 - 680 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 500 - 660 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 510 - 720 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 510 - 710 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 510 - 690 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 510 - 680 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 510 - 660 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 530 - 720 MPa thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire -
- 20 °C Tensile strength of 530 - 710 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 530 - 690 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 530 - 680 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 530 - 660 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 540 - 720 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 540 - 710 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 540 - 690 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 540 - 680 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Tensile strength of 540 - 660 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
Yield strength - Yield strength of 257.3 MPa - - - Predicted Value, RP1
- - Yield strength of 319.9 MPa - - - Predicted Value, RP1 Transverse
- - Yield strength of 430.3 MPa - - - Predicted Value, RP02
- - Yield strength of 438.2 MPa - - - Predicted Value, Transverse
- - Yield strength of 472.8 MPa - - - Predicted Value, RP02 Transverse
- - Yield strength of 515.9 MPa - - - Predicted Value, RP05
- - Yield strength of 516.7 MPa - - - Predicted Value, RP002
- 20 °C Yield strength of 385 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Yield strength of 400 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Yield strength of 410 MPa thermomechanically rolled EN 10025-4, EN 10113-3 Strip, Sheet, Flat, Rod, Wire -
- 20 °C Yield strength of 430 MPa thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire -
- 20 °C Yield strength of 440 MPa thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire -
- 20 °C Yield strength of 460 MPa thermomechanically rolled EN 10113-3, EN 10025-4 Sheet, Strip, Bar, Flat, Rod, Wire -

We are dedicated to helping you achieve success through our reliable steel solutions.

-- Our promise

Similar or equivalent steel materials

Get a quote

Post Categories