Durabor® 22MnB5
Durabor® 22MnB5 introduction
Quenchable boron steel represent a breakthrough in heat treatment technology. This steel uses boron as a hardening agent. The melting and refining process, together with thermomechanical treatment by controlled hot rolling, allow ArcelorMittal quenchable boron steel to attain a remarkable degree of hardness and a very uniform microstructure, resulting in excellent mechanical loading performance after heat treatment of the finished part.
Equivalent material: EN 20MnB5, AFNOR 20MnB5RR, DIN 22B2, BS 174H20, UNI 21B3, UNE 21B3, UNE 20MnB5, JIS 10B21, JIS 15B21, UNS H15211
Durabor® 22MnB5 chemical
| Property |
Value |
Comment |
| Aluminium |
Aluminium of 0.02 % |
min. |
| Boron |
Boron of 0.002 - 0.005 % |
- |
| Carbon |
Carbon of 0.2 - 0.25 % |
- |
| Manganese |
Manganese of 1.1 - 1.4 % |
- |
| Phosphorus |
Phosphorus of 0.025 % |
max. |
| Silicon |
Silicon of 0.15 - 0.35 % |
- |
| Sulfur |
Sulfur of 0.008 % |
max. |
| Titanium |
Titanium of 0.02 - 0.06 % |
- |
Durabor® 22MnB5 electrical
| Property |
- |
- |
| Application areas |
| Chemical composition |
| Delivery condtion |
| Heat Treatment |
| Other |
Specimen heated for 5 minutes at 950°C followed by: |
Endurance limit sD (MPa) |
Spread (sigma) (MPa) |
Maximum stress sD (MPa) |
| Water quenching |
253 |
5 |
562 |
| Oil quenching |
260 |
6 |
578 |
| Water quenching + heat treatment at 200°C for 20 minutes |
293 |
26 |
651 |
Durabor® 22MnB5 mechanical
| Property |
Value |
Comment |
| Elongation |
Elongation of 10 % |
Quenched | 6 mm specimen in the rolling direction |
| - |
Elongation of 27 % |
Delivery condition | 6 mm specimen in the rolling direction |
| Hardness, Rockwell C |
Hardness, Rockwell C of 45 [-] |
Quenched | 6 mm specimen in the rolling direction |
| Tensile strength |
Tensile strength of 520 MPa |
Delivery condition | 6 mm specimen in the rolling direction |
| - |
Tensile strength of 1500 MPa |
Quenched | 6 mm specimen in the rolling direction |
| Yield strength |
Yield strength of 350 MPa |
Delivery condition | 6 mm specimen in the rolling direction |
| - |
Yield strength of 1100 MPa |
Quenched | 6 mm specimen in the rolling direction |
Optimize your operations and streamline productivity with our efficient steel solutions.