DIN EN 10283 Grade 1.4588 Solution Heat Treated
Equivalent material: DIN GX2NiCrMoCuN25-20-6, EN GX2NiCrMoCuN25-20-6, EN 1.4588
DIN EN 10283 Grade 1.4588 Solution Heat Treated general
| Property | Temperature | Value |
|---|---|---|
| Density | 23.0 °C | Density of 8 g/cm³ |
DIN EN 10283 Grade 1.4588 Solution Heat Treated thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Charpy impact energy | 23.0 °C | Charpy impact energy of 60 J | min. |
| Elastic modulus | 23.0 °C | Elastic modulus of 190 - 210 GPa | typical value |
| Elongation | 23.0 °C | Elongation of 30 % | min., A5.65 |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | typical value |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
| Tensile strength | 23.0 °C | Tensile strength of 480 MPa | min. |
| Yield strength Rp0.1 | 23.0 °C | Yield strength Rp0.1 of 235 MPa | min. |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 210 MPa | min. |
DIN EN 10283 Grade 1.4588 Solution Heat Treated chemical
| Property | Value | Comment |
|---|---|---|
| Carbon | Carbon of 0.025 % | max. |
| Chromium | Chromium of 19 - 21 % | - |
| Copper | Copper of 0.5 - 1.5 % | - |
| Iron | - | |
| Manganese | Manganese of 2 % | max |
| Molybdenum | Molybdenum of 6 - 7 % | - |
| Nickel | Nickel of 24 - 26 % | - |
| Nitrogen | Nitrogen of 0.1 - 0.25 % | - |
| Phosphorus | Phosphorus of 0.04 % | max. |
| Silicon | Silicon of 1 % | max. |
| Sulfur | Sulfur of 0.02 % | max. |
DIN EN 10283 Grade 1.4588 Solution Heat Treated magnetic
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
DIN EN 10283 Grade 1.4588 Solution Heat Treated electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 100.0 °C | Coefficient of thermal expansion of 1.65E-5 1/K | mean value between 20°C and the mentioned temperature |
| - | 200.0 °C | Coefficient of thermal expansion of 1.75E-5 1/K | mean value between 20°C and the mentioned temperature |
| - | 300.0 °C | Coefficient of thermal expansion of 1.85E-5 1/K | mean value between 20°C and the mentioned temperature |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 500 J/(kg·K) | - |
| Thermal conductivity | 50.0 °C | Thermal conductivity of 15 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 16 W/(m·K) | - |
DIN EN 10283 Grade 1.4588 Solution Heat Treated mechanical
| Property | Value | Comment |
|---|---|---|
| Thickness | Thickness of 50 mm | max. |
Our steel products are meticulously tested and inspected to ensure utmost reliability.
-- Our promise
Get a quote