DIN 488-1 Grade BSt500S cold formed
DIN 488-1 Grade BSt500S cold formed introduction
BSt 500 S (short: IVS) is a ribbed concrete-reinforcing steel of mean strength (YS: 500 N/mm²) for single rod reinforcing.
The steel wiil also produced as reinforcing wire BSt500 G (smooth) and BSt 500 P (profiled), diameters 4-12 mm.
The weldability is given for the methods metal-arc welding, metal-arc active gas welding, pressure gas welding, flash welding and resistance spot welding.
For high corrosive loads the application of the stainless ribbed reinforcing steel X 6 CrNiMoTi 17 12 2, mat. no. 1.4571, is recommended. Properties acc. DIN 17440.
Equivalent material: DIN 1.0438, DIN B500A, JIS SD490, EN 1.0438
DIN 488-1 Grade BSt500S cold formed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
DIN 488-1 Grade BSt500S cold formed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
DIN 488-1 Grade BSt500S cold formed chemical
| Property |
Value |
| Carbon |
Carbon of 0.22 % |
| Nitrogen |
Nitrogen of 0.01 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Sulfur |
Sulfur of 0.05 % |
DIN 488-1 Grade BSt500S cold formed magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
DIN 488-1 Grade BSt500S cold formed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
DIN 488-1 Grade BSt500S cold formed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A10 |
20.0 °C |
Elongation A10 of 10 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 550 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 500 MPa |
- |