DIN 17465 Grade GX40NiCrSi35-25 cast condition
DIN 17465 Grade GX40NiCrSi35-25 cast condition introduction
G-X 40 NiCrSi 35 25, for parts of oven with highest resistance of scaling, heat resistance and high mechanical loadings, like oven bars, oven rolls, parts for crack oven etc.
resistance:
- in carborising gas: good
- in nitrogenous gas: good
- in oxidising sulfureous gas: middle
- in reductive sulfureous gas: low
- temperature loading on air: 1150°C
Equivalent material: UNI GX50NiCr35-25, ASTM HP, DIN 1.4857, DIN GX40NiCrSi35-26, JIS SCH24, EN GX40NiCrSi35-26, EN 1.4857
DIN 17465 Grade GX40NiCrSi35-25 cast condition general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 8 g/cm³ |
DIN 17465 Grade GX40NiCrSi35-25 cast condition thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
400.0 °C |
Coefficient of thermal expansion of 1.55E-5 1/K |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
| - |
1000.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
| - |
1200.0 °C |
Coefficient of thermal expansion of 1.9E-5 1/K |
| Max service temperature, long |
- |
Max service temperature, long of 0 - 1150 °C |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 14.6 W/(m·K) |
DIN 17465 Grade GX40NiCrSi35-25 cast condition chemical
| Property |
Value |
| Carbon |
Carbon of 0.3 - 0.5 % |
| Chromium |
Chromium of 24 - 26 % |
| Manganese |
Manganese of 1.5 % |
| Nickel |
Nickel of 34 - 36 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 - 2.5 % |
| Sulfur |
Sulfur of 0.03 % |
DIN 17465 Grade GX40NiCrSi35-25 cast condition mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 5 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 440 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 230 MPa |
- |