DIN 17465 Grade GX40CrSi13 soft annealed (+A)
DIN 17465 Grade GX40CrSi13 soft annealed (+A) introduction
G-X 40 CrSi 13, for application as hot plate, dore cases, and other low mechanical loaded compoments of ovens, furthermore for burner nozzle, burner bodys, sliding shoes and slide bars, transport rollers etc.
resistance:
- in oxidising burning atmosphere: 900°C
- in reductive burning atmosphere: 850°C
- in oxidising sulfureous gas: 900°C
- in reductive sulfureous gas: 850°C
Equivalent material: UNI GX35Cr13, JIS SCH1, JIS SCH3, STAS T40SiCr130, MSZ 40CrSi13, DIN 1.4729, UNI GX40CrSi13, EN 1.4729
DIN 17465 Grade GX40CrSi13 soft annealed (+A) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.7 g/cm³ |
DIN 17465 Grade GX40CrSi13 soft annealed (+A) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
400.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.35E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of 0 - 900 °C |
- |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 18.8 W/(m·K) |
- |
DIN 17465 Grade GX40CrSi13 soft annealed (+A) chemical
| Property |
Value |
| Carbon |
Carbon of 0.3 - 0.45 % |
| Chromium |
Chromium of 12 - 14 % |
| Manganese |
Manganese of 0.5 - 1 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 - 2.5 % |
| Sulfur |
Sulfur of 0.03 % |
DIN 17465 Grade GX40CrSi13 soft annealed (+A) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 - 7.5E-7 Ω·m |
Typical for Ferritic Stainless Steel |
DIN 17465 Grade GX40CrSi13 soft annealed (+A) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Ferritic Stainless Steel |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 300 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
Our stringent quality control measures guarantee the highest standards of steel.