DIN 17445 Grade G-X5CrNi13-4 quenched and tempered (+QT1)
DIN 17445 Grade G-X5CrNi13-4 quenched and tempered (+QT1) introduction
G-X 5 CrNi 13 4, for parts in the water power engineering, like water turbine casings and -guidances, for shipbuilding and building of compressores, cold-tough
Equivalent material: ISO C39NiH, DIN 1.4313, DIN X4CrNi13-4, AFNOR Z6CN13-04, BS 425C11, AISI 415, AISI S41500, SAE 415, SAE S41500, JIS SUSF6NM, JIS SCS5, JIS SCS6, EN X3CrNiMo13-4, EN GX5CrNi134, EN 1.4313, ASTM CA6NM, ASTM F6NM, UNS J91540, UNS S41500, UNS S42400
DIN 17445 Grade G-X5CrNi13-4 quenched and tempered (+QT1) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.7 g/cm³ |
DIN 17445 Grade G-X5CrNi13-4 quenched and tempered (+QT1) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.1E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 25 W/(m·K) |
- |
DIN 17445 Grade G-X5CrNi13-4 quenched and tempered (+QT1) chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 % |
| Chromium |
Chromium of 12 - 13.5 % |
| Manganese |
Manganese of 1.5 % |
| Molybdenum |
Molybdenum of 0.7 % |
| Nickel |
Nickel of 3.5 - 5 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.025 % |
DIN 17445 Grade G-X5CrNi13-4 quenched and tempered (+QT1) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
DIN 17445 Grade G-X5CrNi13-4 quenched and tempered (+QT1) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 15 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 240 - 300 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 760 - 960 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 550 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 515 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 500 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 485 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 470 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 455 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 440 MPa |
- |