DIN 17280 Grade 12Ni19 normalized or normalized formed (+N)
  • Home
  • Material
  • DIN 17280 Grade 12Ni19 normalized or normalized formed (+N)

DIN 17280 Grade 12Ni19 normalized or normalized formed (+N)

Equivalent material: EN X12Ni5, DIN 1.5680, AFNOR Z18N5, AISI 2515, SAE 2515, EN 12Ni19, EN 1.5680

DIN 17280 Grade 12Ni19 normalized or normalized formed (+N) general

Property Temperature Value
Density 20.0 °C Density of 7.86 g/cm³

DIN 17280 Grade 12Ni19 normalized or normalized formed (+N) thermal

Property Temperature Value Comment
Coefficient of thermal expansion -100.0 °C Coefficient of thermal expansion of 1.02E-5 1/K -
- 20.0 °C Coefficient of thermal expansion of 1.12E-5 1/K -
- 100.0 °C Coefficient of thermal expansion of 1.17E-5 1/K -
- 200.0 °C Coefficient of thermal expansion of 1.21E-5 1/K -
- 300.0 °C Coefficient of thermal expansion of 1.25E-5 1/K -
- 400.0 °C Coefficient of thermal expansion of 1.28E-5 1/K -
Melting point - Melting point of 1316 - 1595 °C Typical for Nickel Steel
Specific heat capacity -100.0 °C Specific heat capacity of 440 J/(kg·K) -
- 20.0 °C Specific heat capacity of 463 J/(kg·K) -
- 100.0 °C Specific heat capacity of 477 J/(kg·K) -
- 200.0 °C Specific heat capacity of 494 J/(kg·K) -
- 300.0 °C Specific heat capacity of 510 J/(kg·K) -
- 400.0 °C Specific heat capacity of 529 J/(kg·K) -
Thermal conductivity -100.0 °C Thermal conductivity of 29.5 W/(m·K) -
- 20.0 °C Thermal conductivity of 36.2 W/(m·K) -
- 100.0 °C Thermal conductivity of 38.5 W/(m·K) -
- 200.0 °C Thermal conductivity of 39 W/(m·K) -
- 300.0 °C Thermal conductivity of 38.3 W/(m·K) -
- 400.0 °C Thermal conductivity of 36.2 W/(m·K) -
Thermal diffusivity 20.0 °C Thermal diffusivity of 10 mm²/s -
- 100.0 °C Thermal diffusivity of 10 mm²/s -
- 200.0 °C Thermal diffusivity of 9.6 mm²/s -
- 300.0 °C Thermal diffusivity of 8.8 mm²/s -
- 400.0 °C Thermal diffusivity of 7.7 mm²/s -

DIN 17280 Grade 12Ni19 normalized or normalized formed (+N) chemical

Property Value
Carbon Carbon of 0.15 %
Manganese Manganese of 0.3 - 0.8 %
Nickel Nickel of 4.5 - 5.3 %
Phosphorus Phosphorus of 0.03 %
Silicon Silicon of 0.35 %
Sulfur Sulfur of 0.02 %
Vanadium Vanadium of 0.05 %

DIN 17280 Grade 12Ni19 normalized or normalized formed (+N) electrical

Property Temperature Value
Electrical resistivity -100.0 °C Electrical resistivity of 1.95E-7 Ω·m
- 20.0 °C Electrical resistivity of 2.61E-7 Ω·m
- 100.0 °C Electrical resistivity of 3.1E-7 Ω·m
- 200.0 °C Electrical resistivity of 3.78E-7 Ω·m
- 300.0 °C Electrical resistivity of 4.57E-7 Ω·m
- 400.0 °C Electrical resistivity of 5.57E-7 Ω·m

DIN 17280 Grade 12Ni19 normalized or normalized formed (+N) mechanical

Property Temperature Value Comment
Elastic modulus -100.0 °C Elastic modulus of 210 GPa -
- 20.0 °C Elastic modulus of 204 GPa -
- 100.0 °C Elastic modulus of 199 GPa -
- 200.0 °C Elastic modulus of 193 GPa -
- 300.0 °C Elastic modulus of 186 GPa -
- 400.0 °C Elastic modulus of 178 GPa -
Elongation 20.0 °C Elongation of 19 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for Nickel Steel
Shear modulus 23.0 °C Shear modulus of 76 GPa Typical for Nickel Steel
Tensile strength 20.0 °C Tensile strength of 510 - 710 MPa -
Yield strength 20.0 °C Yield strength of 380 - 390 MPa -