DIN 17222 Grade 67SiCr5 cold rolled and hardened
DIN 17222 Grade 67SiCr5 cold rolled and hardened introduction
The steel 67 SiCr 5 is used as cold rolled steel strip for springs with high dimensional accuracy and surface condition up to 3.0 mm thicknesses.
Equivalent material: DIN 1.7103, EN 1.7103
DIN 17222 Grade 67SiCr5 cold rolled and hardened general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.83 g/cm³ |
DIN 17222 Grade 67SiCr5 cold rolled and hardened thermal
| Property | Temperature | Value |
|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.05E-5 1/K |
| - | 20.0 °C | Coefficient of thermal expansion of 1.15E-5 1/K |
| - | 100.0 °C | Coefficient of thermal expansion of 1.21E-5 1/K |
| - | 200.0 °C | Coefficient of thermal expansion of 1.27E-5 1/K |
| - | 300.0 °C | Coefficient of thermal expansion of 1.32E-5 1/K |
| - | 400.0 °C | Coefficient of thermal expansion of 1.36E-5 1/K |
| - | 500.0 °C | Coefficient of thermal expansion of 1.4E-5 1/K |
| - | 600.0 °C | Coefficient of thermal expansion of 1.44E-5 1/K |
| Max service temperature, long | - | Max service temperature, long of 0 - 300 °C |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 423 J/(kg·K) |
| - | 20.0 °C | Specific heat capacity of 461 J/(kg·K) |
| - | 100.0 °C | Specific heat capacity of 479 J/(kg·K) |
| - | 200.0 °C | Specific heat capacity of 499 J/(kg·K) |
| - | 300.0 °C | Specific heat capacity of 517 J/(kg·K) |
| - | 400.0 °C | Specific heat capacity of 536 J/(kg·K) |
| - | 500.0 °C | Specific heat capacity of 558 J/(kg·K) |
| - | 600.0 °C | Specific heat capacity of 587 J/(kg·K) |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 45.1 W/(m·K) |
| - | 100.0 °C | Thermal conductivity of 45.1 W/(m·K) |
| - | 200.0 °C | Thermal conductivity of 44.1 W/(m·K) |
| - | 300.0 °C | Thermal conductivity of 41.9 W/(m·K) |
| - | 400.0 °C | Thermal conductivity of 39.4 W/(m·K) |
| - | 500.0 °C | Thermal conductivity of 36.9 W/(m·K) |
| - | 600.0 °C | Thermal conductivity of 34.4 W/(m·K) |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 12.5 mm²/s |
| - | 100.0 °C | Thermal diffusivity of 11.6 mm²/s |
| - | 200.0 °C | Thermal diffusivity of 10.6 mm²/s |
| - | 300.0 °C | Thermal diffusivity of 9.5 mm²/s |
| - | 400.0 °C | Thermal diffusivity of 8.4 mm²/s |
| - | 500.0 °C | Thermal diffusivity of 7.1 mm²/s |
| - | 600.0 °C | Thermal diffusivity of 5.8 mm²/s |
DIN 17222 Grade 67SiCr5 cold rolled and hardened chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.62 - 0.72 % |
| Chromium | Chromium of 0.4 - 0.6 % |
| Manganese | Manganese of 0.4 - 0.6 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1.2 - 1.4 % |
| Sulfur | Sulfur of 0.035 % |
DIN 17222 Grade 67SiCr5 cold rolled and hardened electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 2.31E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 2.84E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 3.58E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 4.48E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 5.52E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 6.71E-7 Ω·m |
| - | 600.0 °C | Electrical resistivity of 8.06E-7 Ω·m |
DIN 17222 Grade 67SiCr5 cold rolled and hardened mechanical
| Property | Temperature | Value |
|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 217 GPa |
| - | 20.0 °C | Elastic modulus of 206 - 212 GPa |
| - | 100.0 °C | Elastic modulus of 207 GPa |
| - | 200.0 °C | Elastic modulus of 199 GPa |
| - | 300.0 °C | Elastic modulus of 192 GPa |
| - | 400.0 °C | Elastic modulus of 184 GPa |
| - | 500.0 °C | Elastic modulus of 175 GPa |
| - | 600.0 °C | Elastic modulus of 164 GPa |
| Hardness, Vickers | 20.0 °C | Hardness, Vickers of 680 [-] |
| Poisson's ratio | 20.0 °C | Poisson's ratio of 0.28 [-] |
| Shear modulus | 20.0 °C | Shear modulus of 78 GPa |