DIN 17125 Grade StE 355 normalized or normalized formed (+N)
DIN 17125 Grade StE 355 normalized or normalized formed (+N) introduction
The fine grained steel is used acc. DIN 17178 : 1986-5 for welded steel tubes and acc. DIN 17179 : 1986-5 as seamless steel tubes for special purposes down to -20 degrees C.
Application:
pressure vessel construction, apparatus construction, pipelines, mechanical engineering, toolbuilding
Special requirements regarding processing have to be arranged (e.g. coatings). For welded tubes the calculation with the 100 % loads are possible for the seam area.
Equivalent material: DIN 1.0545, DIN S355N, AFNOR S355N, AFNOR E355R, BS S355N, BS 50E, JIS SM50, JIS SM490, EN S355N, EN 1.0545, ISO S355ND, UNS K02803, UNS K12000, UNS K12709
DIN 17125 Grade StE 355 normalized or normalized formed (+N) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.83 g/cm³ |
DIN 17125 Grade StE 355 normalized or normalized formed (+N) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -20 - 400 °C |
- |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
-100.0 °C |
Thermal conductivity of 37.6 W/(m·K) |
- |
| - |
20.0 °C |
Thermal conductivity of 42.2 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 43.2 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 42.9 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.2 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.1 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34.1 W/(m·K) |
- |
| Thermal diffusivity |
-100.0 °C |
Thermal diffusivity of 12.9 mm²/s |
- |
| - |
20.0 °C |
Thermal diffusivity of 11.7 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11.2 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.3 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.4 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.3 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.7 mm²/s |
- |
DIN 17125 Grade StE 355 normalized or normalized formed (+N) chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.2 % |
| Chromium |
Chromium of 0.3 % |
| Copper |
Copper of 0.2 % |
| Manganese |
Manganese of 0.9 - 1.65 % |
| Molybdenum |
Molybdenum of 0.08 % |
| Nickel |
Nickel of 0.3 % |
| Nitrogen |
Nitrogen of 0.02 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.1 - 0.5 % |
| Sulfur |
Sulfur of 0.03 % |
| Vanadium |
Vanadium of 0.1 % |
DIN 17125 Grade StE 355 normalized or normalized formed (+N) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
DIN 17125 Grade StE 355 normalized or normalized formed (+N) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
-100.0 °C |
Electrical resistivity of 1.82E-7 Ω·m |
| - |
20.0 °C |
Electrical resistivity of 2.47E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.96E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.68E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.55E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.56E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.75E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.13E-7 Ω·m |
DIN 17125 Grade StE 355 normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 22 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 20 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 490 - 630 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 490 - 630 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 325 - 355 MPa |
- |
| Yield strength, transverse |
20.0 °C |
Yield strength, transverse of 325 - 355 MPa |
- |
Our state-of-the-art manufacturing ensures precision and impeccable finishes.
-- Our promise