DIN 17111 Grade R10S10 hot rolled
DIN 17111 Grade R10S10 hot rolled introduction
The steel is used for the manufacture of bolts, nuts and rivets (and similar shaped parts).
Equivalent material: DIN 1.0703, EN 1.0703
DIN 17111 Grade R10S10 hot rolled general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
DIN 17111 Grade R10S10 hot rolled thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
| Max service temperature | - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
DIN 17111 Grade R10S10 hot rolled chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.15 % |
| Manganese | Manganese of 0.3 - 0.8 % |
| Phosphorus | Phosphorus of 0.05 % |
| Silicon | Silicon of 0.4 % |
| Sulfur | Sulfur of 0.08 - 0.12 % |
DIN 17111 Grade R10S10 hot rolled magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
DIN 17111 Grade R10S10 hot rolled electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
DIN 17111 Grade R10S10 hot rolled mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
| Shear modulus | 23.0 °C | Shear modulus of 82 GPa | Typical for Low Carbon Steel |
| Tensile strength | 20.0 °C | Tensile strength of 340 - 470 MPa | - |
| Yield strength | 20.0 °C | Yield strength of 215 - 225 MPa | - |