DIN 1681 Grade GS-60 heat treated
DIN 1681 Grade GS-60 heat treated introduction
GS-52 for castings without special stress with good wearing properties, like coatings, bearing rollers, beater heads, hammers. For castings with static or dynamic stress for cog wheels, impellers, sprocket wheels, cranks, baffle plates. Suitable for surface hardening. Application between -10 and +300 °C.
Equivalent material: BDS 45LIII, AFNOR 320-560-M-81, BS A3, GOST 45L-III, ISO 30-57, PN LII600, STAS OT600-3, MSZ Aö.600FK, DIN GE300, DIN 1.0558, EN GE300, EN 1.0558
DIN 1681 Grade GS-60 heat treated general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
DIN 1681 Grade GS-60 heat treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -10 - 300 °C |
- |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 50 W/(m·K) |
- |
DIN 1681 Grade GS-60 heat treated magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
DIN 1681 Grade GS-60 heat treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
DIN 1681 Grade GS-60 heat treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 196 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 15 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 21 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 600 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 300 MPa |
- |