DIN 1651 Grade 60SPb20 cold drawn and stress relieved
DIN 1651 Grade 60SPb20 cold drawn and stress relieved introduction
The fully killed machining steel 60 SPb 20 is used for mass parts of highest strength, especially for lower toughness demands cross-sectional. Its better machinable because of the Pb addition.
Application in the automotive engineering, toolbuilding, apparatus engineering (screws, nuts, smal parts).
Equivalent material: DIN 1.0758, DIN 60 SPb 20, DIN 60SPb22, EN 60SPb20, EN 1.0758
DIN 1651 Grade 60SPb20 cold drawn and stress relieved general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
DIN 1651 Grade 60SPb20 cold drawn and stress relieved thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.18E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
100.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 540 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 600 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 46.5 W/(m·K) |
- |
DIN 1651 Grade 60SPb20 cold drawn and stress relieved chemical
| Property |
Value |
| Carbon |
Carbon of 0.57 - 0.65 % |
| Lead |
Lead of 0.15 - 0.35 % |
| Manganese |
Manganese of 0.7 - 1.1 % |
| Phosphorus |
Phosphorus of 0.06 % |
| Silicon |
Silicon of 0.1 - 0.3 % |
| Sulfur |
Sulfur of 0.18 - 0.25 % |
DIN 1651 Grade 60SPb20 cold drawn and stress relieved electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.3E-7 Ω·m |
DIN 1651 Grade 60SPb20 cold drawn and stress relieved mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 193 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 850 MPa |
- |
Stay ahead of the curve with our advanced steel technologies that push boundaries and unlock new possibilities.