DIN 1.5223 Quenched and Tempered
Equivalent material: DIN 42MnV7, EN 42MnV7, EN 1.5223
DIN 1.5223 Quenched and Tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
typical value |
DIN 1.5223 Quenched and Tempered thermal
| Property |
Temperature |
Value |
Comment |
| Charpy impact energy |
23.0 °C |
Charpy impact energy of 15 - 30 J |
- |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
typical value |
| Elongation |
23.0 °C |
Elongation of 10 - 12 % |
min., A5.65 |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 217 [-] |
max. in soft annealed condition |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
typical value |
| Reduction of area |
23.0 °C |
Reduction of area of 30 - 40 % |
min. |
| Tensile strength |
23.0 °C |
Tensile strength of 880 - 1270 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 685 - 885 MPa |
- |
DIN 1.5223 Quenched and Tempered chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.38 - 0.45 % |
- |
| Iron |
- |
| Manganese |
Manganese of 1.6 - 1.9 % |
- |
| Phosphorus |
Phosphorus of 0.04 % |
max. |
| Silicon |
Silicon of 0.15 - 0.35 % |
- |
| Sulfur |
Sulfur of 0.035 % |
max. |
| Vanadium |
Vanadium of 0.07 - 0.12 % |
- |
DIN 1.5223 Quenched and Tempered electrical
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.33E-5 1/K |
Typical for Manganese Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Manganese Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 510 - 553 J/(kg·K) |
Typical for Manganese Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 16 W/(m·K) |
Typical for Manganese Steel |
DIN 1.5223 Quenched and Tempered mechanical
| Property |
Value |
| Thickness |
Thickness of 16 - 100 mm |