ASTM A989 Grade K31545 Hot Isostatically-Pressed (HIP)
Equivalent material: UNS K31545
ASTM A989 Grade K31545 Hot Isostatically-Pressed (HIP) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Molybdenum Steel |
ASTM A989 Grade K31545 Hot Isostatically-Pressed (HIP) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K |
Typical for Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 502 J/(kg·K) |
Typical for Chromium Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 - 43 W/(m·K) |
Typical for Chromium Molybdenum Steel |
ASTM A989 Grade K31545 Hot Isostatically-Pressed (HIP) chemical
| Property |
Value |
| Carbon |
Carbon of 0.05 - 0.15 % |
| Chromium |
Chromium of 2.7 - 3.3 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Molybdenum |
Molybdenum of 0.8 - 1.06 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.5 % |
| Sulfur |
Sulfur of 0.04 % |
ASTM A989 Grade K31545 Hot Isostatically-Pressed (HIP) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Molybdenum Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 20 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 156 - 207 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 30 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 515 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 310 MPa |
- |