ASTM A982 Grade B Class 1 Quenched and Tempered; Stress-Relieved
ASTM A982 Grade B Class 1 Quenched and Tempered; Stress-Relieved general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.6 - 7.8 g/cm³ | Typical for Ferritic Stainless Steel |
ASTM A982 Grade B Class 1 Quenched and Tempered; Stress-Relieved thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K | Typical for Ferritic Stainless Steel |
| Melting point | - | Melting point of 1425 - 1530 °C | Typical for Ferritic Stainless Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 420 - 586 J/(kg·K) | Typical for Ferritic Stainless Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 11 - 22 W/(m·K) | Typical for Ferritic Stainless Steel |
ASTM A982 Grade B Class 1 Quenched and Tempered; Stress-Relieved chemical
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.025 % |
| Carbon | Carbon of 0.1 - 0.15 % |
| Chromium | Chromium of 11.5 - 13 % |
| Copper | Copper of 0.15 % |
| Manganese | Manganese of 0.25 - 0.8 % |
| Molybdenum | Molybdenum of 0.5 % |
| Nickel | Nickel of 0.75 % |
| Niobium | Niobium of 0.2 % |
| Nitrogen | Nitrogen of 0.08 % |
| Phosphorus | Phosphorus of 0.02 % |
| Silicon | Silicon of 0.5 % |
| Sulfur | Sulfur of 0.015 % |
| Tin | Tin of 0.05 % |
| Titanium | Titanium of 0.05 % |
| Tungsten | Tungsten of 0.1 % |
ASTM A982 Grade B Class 1 Quenched and Tempered; Stress-Relieved electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 6E-7 - 7.5E-7 Ω·m | Typical for Ferritic Stainless Steel |
ASTM A982 Grade B Class 1 Quenched and Tempered; Stress-Relieved mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Charpy impact energy | 23.0 °C | Charpy impact energy of 40 J | - |
| Elastic modulus | 23.0 °C | Elastic modulus of 220 GPa | Typical for Ferritic Stainless Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 18 % | - |
| Hardness, Brinell | 23.0 °C | Hardness, Brinell of 269 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Ferritic Stainless Steel |
| Reduction of area | 23.0 °C | Reduction of area of 50 % | - |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Ferritic Stainless Steel |
| Tensile strength | 23.0 °C | Tensile strength of 760 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 620 MPa | - |