ASTM A958 Grade SC4130 Class 65/35, Heat-Treated
Equivalent material: DIN 1.7230, DIN GS-34CrMo4, DIN G34CrMo4, EN 1.7230, ISO G32CrMo4, ASTM Grade SC4130
ASTM A958 Grade SC4130 Class 65/35, Heat-Treated general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Molybdenum Steel |
ASTM A958 Grade SC4130 Class 65/35, Heat-Treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K |
Typical for Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 448 - 502 J/(kg·K) |
Typical for Chromium Molybdenum Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 36 - 43 W/(m·K) |
Typical for Chromium Molybdenum Steel |
ASTM A958 Grade SC4130 Class 65/35, Heat-Treated chemical
| Property |
Value |
| Carbon |
Carbon of 0.28 - 0.33 % |
| Chromium |
Chromium of 0.8 - 1.1 % |
| Manganese |
Manganese of 0.4 - 0.8 % |
| Molybdenum |
Molybdenum of 0.15 - 0.25 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.3 - 0.6 % |
| Sulfur |
Sulfur of 0.04 % |
ASTM A958 Grade SC4130 Class 65/35, Heat-Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Molybdenum Steel |
| Elongation A50 |
20.0 °C |
Elongation A50 of 24 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 35 % |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 450 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 240 MPa |
- |