ASTM A871 Type II Grade 60 As-Rolled, Normalized or Quenched and Tempered
Equivalent material: ASTM Type II Grade 65, ASTM Type II Grade 60
ASTM A871 Type II Grade 60 As-Rolled, Normalized or Quenched and Tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A871 Type II Grade 60 As-Rolled, Normalized or Quenched and Tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
ASTM A871 Type II Grade 60 As-Rolled, Normalized or Quenched and Tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.2 % |
| Chromium |
Chromium of 0.4 - 0.7 % |
| Copper |
Copper of 0.2 - 0.4 % |
| Manganese |
Manganese of 0.75 - 1.35 % |
| Nickel |
Nickel of 0.5 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.5 % |
| Sulfur |
Sulfur of 0.03 % |
| Vanadium |
Vanadium of 0.01 - 0.1 % |
ASTM A871 Type II Grade 60 As-Rolled, Normalized or Quenched and Tempered magnetic
| Property |
Temperature |
Value |
Comment |
| Curie temperature |
20.0 °C |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A871 Type II Grade 60 As-Rolled, Normalized or Quenched and Tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A871 Type II Grade 60 As-Rolled, Normalized or Quenched and Tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Charpy impact energy |
20.0 °C |
Charpy impact energy of 20 J |
- |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A200 |
20.0 °C |
Elongation A200 of 16 % |
- |
| Elongation A50 |
20.0 °C |
Elongation A50 of 18 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 520 MPa |
- |
| Yield Strength Rp0.2, short transverse |
20.0 °C |
Yield Strength Rp0.2, short transverse of 415 MPa |
- |
Our steel embodies these qualities to deliver exceptional results.
-- Our promise