ASTM A841 Grade A Class 1 Thermo-Mechanical Control Process (TMCP)
ASTM A841 Grade A Class 1 Thermo-Mechanical Control Process (TMCP) general
| Property | Value | Comment |
|---|---|---|
| Density | Density of 7.6 - 7.7 g/cm³ | Typical for Martensitic Stainless Steel |
ASTM A841 Grade A Class 1 Thermo-Mechanical Control Process (TMCP) thermal
| Property | Value | Comment |
|---|---|---|
| Coefficient of thermal expansion | Coefficient of thermal expansion of 1e-05 - 1.5e-05 1/K | Typical for Martensitic Stainless Steel |
| Melting point | Melting point of 1370 - 1530 °C | Typical for Martensitic Stainless Steel |
| Specific heat capacity | Specific heat capacity of 460 J/(kg·K) | Typical for Martensitic Stainless Steel |
| Thermal conductivity | Thermal conductivity of 14 - 31 W/(m·K) | Typical for Martensitic Stainless Steel |
ASTM A841 Grade A Class 1 Thermo-Mechanical Control Process (TMCP) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Aluminium | Aluminium of 0.02 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Carbon | Carbon of 0.2 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Chromium | Chromium of 0.25 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Copper | Copper of 0.35 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Manganese | Manganese of 0.7 - 1.35 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Molybdenum | Molybdenum of 0.08 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Nickel | Nickel of 0.25 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Niobium | Niobium of 0.03 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Phosphorus | Phosphorus of 0.03 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Silicon | Silicon of 0.15 - 0.5 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Sulfur | Sulfur of 0.03 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Vanadium | Vanadium of 0.06 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
ASTM A841 Grade A Class 1 Thermo-Mechanical Control Process (TMCP) electrical
| Property | Value | Comment |
|---|---|---|
| Electrical conductivity | Electrical conductivity of 7 S/m | Predicted Value |
| Electrical resistivity | Electrical resistivity of 6e-07 Ω·m | Typical for Martensitic Stainless Steel |
ASTM A841 Grade A Class 1 Thermo-Mechanical Control Process (TMCP) mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
| Elastic modulus | Elastic modulus of 220 GPa | - | - | - | Typical for Martensitic Stainless Steel |
| Elongation | Elongation of 17.5 % | - | - | - | Predicted Value, A80 |
| - | Elongation of 18 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | A200 |
| - | Elongation of 19.4 % | - | - | - | Predicted Value, Transverse |
| - | Elongation of 20.0 % | - | - | - | Predicted Value, A80 Transverse |
| - | Elongation of 22 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | A50 |
| - | Elongation of 24.7 % | - | - | - | Predicted Value |
| Poisson's ratio | Poisson's ratio of 0.3 [-] | - | - | - | Typical for Martensitic Stainless Steel |
| Reduction of area | Reduction of area of 39.7 % | - | - | - | Predicted Value |
| - | Reduction of area of 43.5 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | Shear modulus of 77 GPa | - | - | - | Typical for Martensitic Stainless Steel |
| Shear strength | Shear strength of 516.5 MPa | - | - | - | Predicted Value |
| Tensile strength | Tensile strength of 450 - 585 MPa | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | - |
| - | Tensile strength of 485 - 620 MPa | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | - |
| Yield strength | Yield strength of 266.6 MPa | - | - | - | Predicted Value, RP1 |
| - | Yield strength of 310 MPa | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | - |
| - | Yield strength of 316.7 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | Yield strength of 345 MPa | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | - |
| - | Yield strength of 353.7 MPa | - | - | - | Predicted Value, Transverse |
| - | Yield strength of 370.7 MPa | - | - | - | Predicted Value, RP05 |
| - | Yield strength of 371.3 MPa | - | - | - | Predicted Value, RP02 |
| - | Yield strength of 405.4 MPa | - | - | - | Predicted Value, RP002 |
| - | Yield strength of 454 MPa | - | - | - | Predicted Value, RP02 Transverse |