ASTM A841 Grade B Class 1 Thermo-Mechanical Control Process (TMCP)
ASTM A841 Grade B Class 1 Thermo-Mechanical Control Process (TMCP) general
| Property | Value | Comment |
|---|---|---|
| Density | Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
ASTM A841 Grade B Class 1 Thermo-Mechanical Control Process (TMCP) thermal
| Property | Value | Comment |
|---|---|---|
| Coefficient of thermal expansion | Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K | Typical for Low Carbon Steel |
| Max service temperature | Max service temperature of 303.3 °C | Predicted Value, Long |
| - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
| Thermal conductivity | Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
ASTM A841 Grade B Class 1 Thermo-Mechanical Control Process (TMCP) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Aluminium | Aluminium of 0.02 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Carbon | Carbon of 0.15 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Chromium | Chromium of 0.25 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Copper | Copper of 0.35 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Manganese | Manganese of 0.7 - 1.35 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Molybdenum | Molybdenum of 0.3 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Nickel | Nickel of 0.6 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Niobium | Niobium of 0.03 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Phosphorus | Phosphorus of 0.03 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Silicon | Silicon of 0.15 - 0.5 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Sulfur | Sulfur of 0.025 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
| Vanadium | Vanadium of 0.06 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate |
ASTM A841 Grade B Class 1 Thermo-Mechanical Control Process (TMCP) magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
ASTM A841 Grade B Class 1 Thermo-Mechanical Control Process (TMCP) electrical
| Property | Value | Comment |
|---|---|---|
| Electrical conductivity | Electrical conductivity of 6 S/m | Predicted Value |
| Electrical resistivity | Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | Typical for Carbon Steel |
ASTM A841 Grade B Class 1 Thermo-Mechanical Control Process (TMCP) mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
| Elastic modulus | Elastic modulus of 200 - 215 GPa | - | - | - | Typical for Low Carbon Steel |
| Elongation | Elongation of 17.2 % | - | - | - | Predicted Value, A80 |
| - | Elongation of 18 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | A200 |
| - | Elongation of 19.2 % | - | - | - | Predicted Value, Transverse |
| - | Elongation of 20.0 % | - | - | - | Predicted Value, A80 Transverse |
| - | Elongation of 22 % | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | A50 |
| - | Elongation of 24.9 % | - | - | - | Predicted Value |
| Hardness, Brinell | Hardness, Brinell of 243 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | Poisson's ratio of 0.29 [-] | - | - | - | Typical for Low Carbon Steel |
| Reduction of area | Reduction of area of 40.1 % | - | - | - | Predicted Value |
| - | Reduction of area of 44.1 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | Shear modulus of 82 GPa | - | - | - | Typical for Low Carbon Steel |
| Shear strength | Shear strength of 553.7 MPa | - | - | - | Predicted Value |
| Tensile strength | Tensile strength of 450 - 585 MPa | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | - |
| - | Tensile strength of 485 - 620 MPa | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | - |
| Yield strength | Yield strength of 263.7 MPa | - | - | - | Predicted Value, RP1 |
| - | Yield strength of 310 MPa | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | - |
| - | Yield strength of 317.9 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | Yield strength of 345 MPa | Thermo-Mechanical Control Process (TMCP) | ASTM A841 | Plate | - |
| - | Yield strength of 366.4 MPa | - | - | - | Predicted Value, Transverse |
| - | Yield strength of 368.8 MPa | - | - | - | Predicted Value, RP02 |
| - | Yield strength of 373.8 MPa | - | - | - | Predicted Value, RP05 |
| - | Yield strength of 407.4 MPa | - | - | - | Predicted Value, RP002 |
| - | Yield strength of 462.1 MPa | - | - | - | Predicted Value, RP02 Transverse |