ASTM A789 Grade S32950 Heat-Treated
Equivalent material: AISI S32950, SAE S32950, UNS S32950
ASTM A789 Grade S32950 Heat-Treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Duplex Stainless Steel |
ASTM A789 Grade S32950 Heat-Treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 1/K |
Typical for Duplex Stainless Steel |
| Max service temperature |
- |
Max service temperature of 300 °C |
Typical for Duplex Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Duplex Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 - 502 J/(kg·K) |
Typical for Duplex Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 13 - 30 W/(m·K) |
Typical for Duplex Stainless Steel |
ASTM A789 Grade S32950 Heat-Treated chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 26 - 29 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 1 - 2.5 % |
| Nickel |
Nickel of 3.5 - 5.2 % |
| Nitrogen |
Nitrogen of 0.15 - 0.35 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.01 % |
ASTM A789 Grade S32950 Heat-Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
Typical for Duplex Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 20 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 290 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 30 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 290 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Duplex Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Duplex Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 690 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 480 MPa |
- |