ASTM A709 Grade HPS 485W Quenched and Tempered
ASTM A709 Grade HPS 485W Quenched and Tempered general
| Property | Value | Comment |
|---|---|---|
| Density | Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
ASTM A709 Grade HPS 485W Quenched and Tempered thermal
| Property | Value | Comment |
|---|---|---|
| Coefficient of thermal expansion | Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K | Typical for Low Carbon Steel |
| Max service temperature | Max service temperature of 326.5 °C | Predicted Value, Long |
| - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
| Thermal conductivity | Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
ASTM A709 Grade HPS 485W Quenched and Tempered magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
ASTM A709 Grade HPS 485W Quenched and Tempered electrical
| Property | Value | Comment |
|---|---|---|
| Electrical conductivity | Electrical conductivity of 8 S/m | Predicted Value |
| Electrical resistivity | Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | Typical for Carbon Steel |
ASTM A709 Grade HPS 485W Quenched and Tempered mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
| Elastic modulus | Elastic modulus of 200 - 215 GPa | - | - | - | Typical for Low Carbon Steel |
| Elongation | Elongation of 10.1 % | - | - | - | Predicted Value, A200 |
| - | Elongation of 16.2 % | - | - | - | Predicted Value, A80 |
| - | Elongation of 19 % | Quenched and Tempered | ASTM A709 | Plate, Bar | A50 |
| - | Elongation of 19.6 % | - | - | - | Predicted Value, A80 Transverse |
| - | Elongation of 20.5 % | - | - | - | Predicted Value, Transverse |
| - | Elongation of 22.8 % | - | - | - | Predicted Value |
| Poisson's ratio | Poisson's ratio of 0.29 [-] | - | - | - | Typical for Low Carbon Steel |
| Reduction of area | Reduction of area of 42.9 % | - | - | - | Predicted Value, Transverse |
| - | Reduction of area of 45.7 % | - | - | - | Predicted Value |
| Shear modulus | Shear modulus of 82 GPa | - | - | - | Typical for Low Carbon Steel |
| Shear strength | Shear strength of 644.8 MPa | - | - | - | Predicted Value |
| Tensile strength | Tensile strength of 585 - 760 MPa | Quenched and Tempered | ASTM A709 | Plate, Bar | - |