ASTM A705 Grade XM-16 Age-Hardening H1000
Equivalent material: DIN 1.4543, DIN X3CrNiCuTi12-9, DIN X3CrNiCuTiNb12-9, AISI S45500, AISI XM-16, SAE S45500, SAE XM-16, EN 1.4543, UNS S45500
ASTM A705 Grade XM-16 Age-Hardening H1000 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
ASTM A705 Grade XM-16 Age-Hardening H1000 chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 11 - 12.5 % |
| Copper |
Copper of 1.5 - 2.5 % |
| Manganese |
Manganese of 0.5 % |
| Molybdenum |
Molybdenum of 0.5 % |
| Nickel |
Nickel of 7.5 - 9.5 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.5 % |
| Sulfur |
Sulfur of 0.015 % |
| Titanium |
Titanium of 0.9 - 1.4 % |
ASTM A705 Grade XM-16 Age-Hardening H1000 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 10 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 363 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 40 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 40 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 1410 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 1280 MPa |
- |