ASTM A705 Grade XM-12 Age-Hardening H1100
Equivalent material: DIN 1.4545, DIN X5CrNiCuNb15-5, DIN 1.4545.4, DIN 1.4545.9, AISI XM-12, SAE XM-12, EN X5CrNiCu15-5, EN 1.4545, ASTM CB7Cu-2, UNS J92110
ASTM A705 Grade XM-12 Age-Hardening H1100 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
ASTM A705 Grade XM-12 Age-Hardening H1100 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
ASTM A705 Grade XM-12 Age-Hardening H1100 chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 % |
| Chromium |
Chromium of 14 - 15.5 % |
| Copper |
Copper of 2.5 - 4.5 % |
| Manganese |
Manganese of 1 % |
| Nickel |
Nickel of 3.5 - 5.5 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A705 Grade XM-12 Age-Hardening H1100 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
ASTM A705 Grade XM-12 Age-Hardening H1100 mechanical
| Property |
Temperature |
Value |
Comment |
| Charpy impact energy |
23.0 °C |
Charpy impact energy of 20 - 34 J |
- |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 10 - 14 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 302 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 31 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 29 - 45 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 965 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 795 MPa |
- |