ASTM A705 Grade 632 Age-Hardening RH950
Equivalent material: UNS S15700
ASTM A705 Grade 632 Age-Hardening RH950 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
ASTM A705 Grade 632 Age-Hardening RH950 chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.75 - 1.5 % |
| Carbon |
Carbon of 0.09 % |
| Chromium |
Chromium of 14 - 16 % |
| Manganese |
Manganese of 1 % |
| Molybdenum |
Molybdenum of 2 - 3 % |
| Nickel |
Nickel of 6.5 - 7.75 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A705 Grade 632 Age-Hardening RH950 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 7 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 415 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 38 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 25 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 1380 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 1210 MPa |
- |