ASTM A681 Grade Type O2 Annealed
Equivalent material: DIN 1.2842, DIN 90MnCrV8, AFNOR 90MnCrV8, BS BO2, BS 90MnCrV8, UNI 88MnV8KU, AISI O2, SAE O2, EN 90MnCrV8, EN 90MnV8, EN 1.2842, ISO 90MnCrV8, GOST 9G2F, GB/T 9Mn2V, GB/T T20000, UNS T31502
ASTM A681 Grade Type O2 Annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.72 - 8 g/cm³ |
Typical for Tool And Machining Steel |
ASTM A681 Grade Type O2 Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.3E-5 1/K |
Typical for Tool And Machining Steel |
| Melting point |
- |
Melting point of 1370 - 1425 °C |
Typical for Tool And Machining Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 460 J/(kg·K) |
Typical for Tool And Machining Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 17 - 42 W/(m·K) |
Typical for Tool And Machining Steel |
ASTM A681 Grade Type O2 Annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.85 - 0.95 % |
| Chromium |
Chromium of 0.5 % |
| Manganese |
Manganese of 1.4 - 1.8 % |
| Molybdenum |
Molybdenum of 0.3 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.5 % |
| Sulfur |
Sulfur of 0.03 % |
| Vanadium |
Vanadium of 0.3 % |
ASTM A681 Grade Type O2 Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 203 - 211 GPa |
Typical for Tool And Machining Steel |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 217 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Tool And Machining Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 79 GPa |
Typical for Tool And Machining Steel |