ASTM A681 Grade Type O1 Annealed
Equivalent material: DIN 1.2510, DIN 100MnCrW4, AFNOR 90MWCV5, BS BO 1, UNE F.522.A, UNE F.5220, AISI O1, SAE O1, JIS SKS3, EN 100MnCrW4, EN 1.2510, ISO 100MnCrW4, GOST 95ChWG, GB/T 9CrWMn, GB/T T20110, GB/T 9Cr06WMn, UNS T31501
ASTM A681 Grade Type O1 Annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.72 - 8 g/cm³ |
Typical for Tool And Machining Steel |
ASTM A681 Grade Type O1 Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.3E-5 1/K |
Typical for Tool And Machining Steel |
| Melting point |
- |
Melting point of 1370 - 1425 °C |
Typical for Tool And Machining Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 460 J/(kg·K) |
Typical for Tool And Machining Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 17 - 42 W/(m·K) |
Typical for Tool And Machining Steel |
ASTM A681 Grade Type O1 Annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.85 - 1 % |
| Chromium |
Chromium of 0.4 - 0.7 % |
| Manganese |
Manganese of 1 - 1.4 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.1 - 0.5 % |
| Sulfur |
Sulfur of 0.03 % |
| Tungsten |
Tungsten of 0.4 - 0.6 % |
| Vanadium |
Vanadium of 0.3 % |
ASTM A681 Grade Type O1 Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 203 - 211 GPa |
Typical for Tool And Machining Steel |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 212 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Tool And Machining Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 79 GPa |
Typical for Tool And Machining Steel |