ASTM A653 BHS Grade 300
Equivalent material: DIN 1.0930, EN HX300BD, EN 1.0930
ASTM A653 BHS Grade 300 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Manganese Steel |
ASTM A653 BHS Grade 300 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.33E-5 1/K |
Typical for Manganese Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Manganese Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 510 - 553 J/(kg·K) |
Typical for Manganese Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 16 W/(m·K) |
Typical for Manganese Steel |
ASTM A653 BHS Grade 300 chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 % |
| Chromium |
Chromium of 0.15 % |
| Copper |
Copper of 0.2 % |
| Manganese |
Manganese of 1.5 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 0.2 % |
| Niobium |
Niobium of 8E-3 % |
| Phosphorus |
Phosphorus of 0.12 % |
| Sulfur |
Sulfur of 0.03 % |
| Titanium |
Titanium of 0.03 % |
| Vanadium |
Vanadium of 8E-3 % |
ASTM A653 BHS Grade 300 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Manganese Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 20 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Manganese Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 390 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 300 MPa |
- |
Our durable steel materials redefine durability, delivering long-lasting performance and reliability.
-- Our promise
Similar or equivalent steel materials
- EN 10292 Grade HX300BD +Z, +ZF, +ZA, +AZ, +AS,hot rolled or cold rolled, hot dip coated
- EN 10292 Grade HX300BD hot rolled or cold rolled, hot dip coated,+Z, +ZF, +ZA, +AZ, +AS
- ASTM A1008 BHS Grade 300 Bake-Hardenable