ASTM A592 Grade A Quenched and Tempered
ASTM A592 Grade A Quenched and Tempered general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
ASTM A592 Grade A Quenched and Tempered thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
| Max service temperature | - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
ASTM A592 Grade A Quenched and Tempered chemical
| Property | Value |
|---|---|
| Boron | Boron of 2.5E-3 % |
| Carbon | Carbon of 0.15 - 0.21 % |
| Chromium | Chromium of 0.5 - 0.8 % |
| Manganese | Manganese of 0.8 - 1.1 % |
| Molybdenum | Molybdenum of 0.18 - 0.28 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 0.4 - 0.8 % |
| Sulfur | Sulfur of 0.025 % |
| Zirconium | Zirconium of 0.05 - 0.15 % |
ASTM A592 Grade A Quenched and Tempered magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
ASTM A592 Grade A Quenched and Tempered electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
ASTM A592 Grade A Quenched and Tempered mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 17 - 18 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
| Reduction of area | 23.0 °C | Reduction of area of 40 - 45 % | - |
| Shear modulus | 23.0 °C | Shear modulus of 82 GPa | Typical for Low Carbon Steel |
| Tensile strength | 23.0 °C | Tensile strength of 725 - 930 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 620 - 690 MPa | - |