ASTM A573 Grade 400
ASTM A573 Grade 400 general
| Property | Value | Comment |
|---|---|---|
| Density | Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
ASTM A573 Grade 400 thermal
| Property | Value | Comment |
|---|---|---|
| Coefficient of thermal expansion | Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K | Typical for Low Carbon Steel |
| Max service temperature | Max service temperature of 315.4 °C | Predicted Value, Long |
| - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
| Thermal conductivity | Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
ASTM A573 Grade 400 chemical
| Property | Value | Related Standards |
|---|---|---|
| Carbon | Carbon of 0.23 % | ASTM A573 |
| Manganese | Manganese of 0.6 - 0.9 % | ASTM A573 |
| Phosphorus | Phosphorus of 0.03 % | ASTM A573 |
| Silicon | Silicon of 0.1 - 0.35 % | ASTM A573 |
| Sulfur | Sulfur of 0.03 % | ASTM A573 |
ASTM A573 Grade 400 magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
ASTM A573 Grade 400 electrical
| Property | Value | Comment |
|---|---|---|
| Electrical conductivity | Electrical conductivity of 7 S/m | Predicted Value |
| Electrical resistivity | Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | Typical for Carbon Steel |
ASTM A573 Grade 400 mechanical
| Property | Value | Comment |
|---|---|---|
| Elastic modulus | Elastic modulus of 200 - 215 GPa | Typical for Low Carbon Steel |
| Elongation | Elongation of 15.0 % | Predicted Value, A200 |
| - | Elongation of 15.4 % | Predicted Value, A80 |
| - | Elongation of 18.3 % | Predicted Value, Transverse |
| - | Elongation of 20.2 % | Predicted Value, A80 Transverse |
| - | Elongation of 20.6 % | Predicted Value, A5 |
| - | Elongation of 21 % | Predicted Value, A50 |
| - | Elongation of 21.6 % | Predicted Value |
| Poisson's ratio | Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
| Reduction of area | Reduction of area of 42.1 % | Predicted Value |
| - | Reduction of area of 43.0 % | Predicted Value, Transverse |
| Shear modulus | Shear modulus of 82 GPa | Typical for Low Carbon Steel |
| Shear strength | Shear strength of 511.2 MPa | Predicted Value |