ASTM A565 Grade XM-32 Heat treated for high-temperature service
Equivalent material: DIN 1.4938, DIN 1.4939, DIN 1.4933, EN X12CrNiMoN12, EN 1.4938, EN 1.4939, EN 1.4933, UNS S64152
ASTM A565 Grade XM-32 Heat treated for high-temperature service general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
ASTM A565 Grade XM-32 Heat treated for high-temperature service thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
ASTM A565 Grade XM-32 Heat treated for high-temperature service chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 - 0.15 % |
| Chromium |
Chromium of 11 - 12.5 % |
| Manganese |
Manganese of 0.5 - 0.9 % |
| Molybdenum |
Molybdenum of 1.5 - 2 % |
| Nickel |
Nickel of 2 - 3 % |
| Nitrogen |
Nitrogen of 0.01 - 0.05 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.35 % |
| Sulfur |
Sulfur of 0.025 % |
| Vanadium |
Vanadium of 0.25 - 0.4 % |
ASTM A565 Grade XM-32 Heat treated for high-temperature service electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
ASTM A565 Grade XM-32 Heat treated for high-temperature service mechanical
| Property |
Temperature |
Value |
Comment |
| Charpy impact energy |
23.0 °C |
Charpy impact energy of 40 J |
- |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 15 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 302 - 352 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 30 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 1000 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 795 MPa |
- |
Drive progress and development with our high-performance steel materials.