ASTM A564 Grade XM-12 H900
Equivalent material: DIN 1.4545, DIN X5CrNiCuNb15-5, DIN 1.4545.4, DIN 1.4545.9, AISI XM-12, SAE XM-12, EN X5CrNiCu15-5, EN 1.4545, ASTM CB7Cu-2, UNS J92110
ASTM A564 Grade XM-12 H900 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
ASTM A564 Grade XM-12 H900 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
ASTM A564 Grade XM-12 H900 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
ASTM A564 Grade XM-12 H900 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 10 % |
- |
| Elongation A50, transverse |
23.0 °C |
Elongation A50, transverse of 6 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 388 [-] |
- |
| Hardness, Brinell, trans |
23.0 °C |
Hardness, Brinell, trans of 388 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 40 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 35 % |
- |
| Reduction of area, transverse |
23.0 °C |
Reduction of area, transverse of 15 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 1310 MPa |
- |
| Tensile strength, transverse |
23.0 °C |
Tensile strength, transverse of 1310 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 1170 MPa |
- |
| Yield strength Rp0.2, transverse |
23.0 °C |
Yield strength Rp0.2, transverse of 1170 MPa |
- |