ASTM A564 Grade S46500 H1000
Equivalent material: UNS S46500
ASTM A564 Grade S46500 H1000 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
ASTM A564 Grade S46500 H1000 chemical
| Property |
Value |
| Carbon |
Carbon of 0.02 % |
| Chromium |
Chromium of 11 - 12.5 % |
| Manganese |
Manganese of 0.25 % |
| Molybdenum |
Molybdenum of 0.75 - 1.25 % |
| Nickel |
Nickel of 10.75 - 11.25 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.25 % |
| Sulfur |
Sulfur of 0.01 % |
| Titanium |
Titanium of 1.5 - 1.8 % |
ASTM A564 Grade S46500 H1000 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 10 % |
- |
| Elongation A50, transverse |
23.0 °C |
Elongation A50, transverse of 10 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 430 [-] |
- |
| Hardness, Brinell, trans |
23.0 °C |
Hardness, Brinell, trans of 430 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 45 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 50 % |
- |
| Reduction of area, transverse |
23.0 °C |
Reduction of area, transverse of 40 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 1515 MPa |
- |
| Tensile strength, transverse |
23.0 °C |
Tensile strength, transverse of 1515 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 1380 MPa |
- |
| Yield strength Rp0.2, transverse |
23.0 °C |
Yield strength Rp0.2, transverse of 1380 MPa |
- |