ASTM A551 Class BHT Heat-Treated
ASTM A551 Class BHT Heat-Treated general
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | Density of 7.8 - 7.9 g/cm³ | Typical for High Carbon Steel |
ASTM A551 Class BHT Heat-Treated thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1.32E-5 1/K | Typical for High Carbon Steel |
Max service temperature | - | Max service temperature of 500 °C | Typical for Carbon Steel |
Melting point | - | Melting point of 1289 - 1478 °C | Typical for High Carbon Steel |
Specific heat capacity | 23.0 °C | Specific heat capacity of 486 J/(kg·K) | Typical for High Carbon Steel |
Thermal conductivity | 23.0 °C | Thermal conductivity of 36 W/(m·K) | Typical for High Carbon Steel |
ASTM A551 Class BHT Heat-Treated chemical
Property | Value |
---|---|
Aluminium | Aluminium of 0.06 % |
Carbon | Carbon of 0.6 - 0.75 % |
Chromium | Chromium of 0.25 % |
Copper | Copper of 0.35 % |
Manganese | Manganese of 0.6 - 0.9 % |
Molybdenum | Molybdenum of 0.1 % |
Nickel | Nickel of 0.25 % |
Niobium | Niobium of 0.05 % |
Phosphorus | Phosphorus of 0.03 % |
Silicon | Silicon of 0.15 - 1 % |
Sulfur | Sulfur of 0.005 - 0.04 % |
Titanium | Titanium of 0.03 % |
Vanadium | Vanadium of 0.04 % |
ASTM A551 Class BHT Heat-Treated electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Electrical resistivity | 23.0 °C | Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
ASTM A551 Class BHT Heat-Treated mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | Elastic modulus of 200 - 215 GPa | Typical for High Carbon Steel |
Elongation A50 | 23.0 °C | Elongation A50 of 14 % | - |
Hardness, Brinell | 23.0 °C | Hardness, Brinell of 255 - 302 [-] | - |
Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for High Carbon Steel |
Reduction of area | 23.0 °C | Reduction of area of 28 % | - |
Shear modulus | 23.0 °C | Shear modulus of 81 GPa | Typical for High Carbon Steel |
Tensile strength | 23.0 °C | Tensile strength of 860 MPa | - |