ASTM A543 Class 1 Type C Quenched and Tempered
ASTM A543 Class 1 Type C Quenched and Tempered general
| Property | Value | Comment |
|---|---|---|
| Density | Density of 7.8 g/cm³ | Typical for Steel |
ASTM A543 Class 1 Type C Quenched and Tempered thermal
| Property | Value | Comment |
|---|---|---|
| Coefficient of thermal expansion | Coefficient of thermal expansion of 11.88 1/K | Predicted Value |
| Specific heat capacity | Specific heat capacity of 458.4 J/(kg·K) | Predicted Value |
| Thermal conductivity | Thermal conductivity of 31.3 W/(m·K) | Predicted Value |
ASTM A543 Class 1 Type C Quenched and Tempered chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Carbon | Carbon of 0.18 % | Quenched and Tempered | ASTM A543 | Plate |
| Chromium | Chromium of 1 - 1.9 % | Quenched and Tempered | ASTM A543 | Plate |
| Manganese | Manganese of 0.4 % | Quenched and Tempered | ASTM A543 | Plate |
| Molybdenum | Molybdenum of 0.2 - 0.65 % | Quenched and Tempered | ASTM A543 | Plate |
| Nickel | Nickel of 2 - 3.5 % | Quenched and Tempered | ASTM A543 | Plate |
| Phosphorus | Phosphorus of 0.02 % | Quenched and Tempered | ASTM A543 | Plate |
| Silicon | Silicon of 0.15 - 0.4 % | Quenched and Tempered | ASTM A543 | Plate |
| Sulfur | Sulfur of 0.02 % | Quenched and Tempered | ASTM A543 | Plate |
ASTM A543 Class 1 Type C Quenched and Tempered electrical
| Property | Value | Comment |
|---|---|---|
| Electrical conductivity | Electrical conductivity of 3 S/m | Predicted Value |
| Electrical resistivity | Electrical resistivity of 37 Ω·m | Predicted Value |
ASTM A543 Class 1 Type C Quenched and Tempered mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
| Elastic modulus | Elastic modulus of 190 - 210 GPa | - | - | - | Typical for Steel |
| Elongation | Elongation of 12.6 % | - | - | - | Predicted Value, A200 |
| - | Elongation of 14 % | Quenched and Tempered | ASTM A543 | Plate | A50 |
| - | Elongation of 16.9 % | - | - | - | Predicted Value, A80 |
| - | Elongation of 18.4 % | - | - | - | Predicted Value, Transverse |
| - | Elongation of 20.2 % | - | - | - | Predicted Value, A80 Transverse |
| - | Elongation of 20.5 % | - | - | - | Predicted Value |
| Poisson's ratio | Poisson's ratio of 0.3 [-] | - | - | - | Typical for Steel |
| Reduction of area | Reduction of area of 43.5 % | - | - | - | Predicted Value, Transverse |
| - | Reduction of area of 44.8 % | - | - | - | Predicted Value |
| Shear modulus | Shear modulus of 79.4 GPa | - | - | - | Predicted Value |
| Shear strength | Shear strength of 618.5 MPa | - | - | - | Predicted Value |
| Tensile strength | Tensile strength of 725 - 860 MPa | Quenched and Tempered | ASTM A543 | Plate | - |
| Yield strength | Yield strength of 315.9 MPa | - | - | - | Predicted Value, RP1 |
| - | Yield strength of 330.7 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | Yield strength of 332.5 MPa | - | - | - | Predicted Value, RP05 |
| - | Yield strength of 490 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | Yield strength of 494.6 MPa | - | - | - | Predicted Value, Transverse |
| - | Yield strength of 585 MPa | Quenched and Tempered | ASTM A543 | Plate | - |
| - | Yield strength of 594.3 MPa | - | - | - | Predicted Value, RP02 |
| - | Yield strength of 666.4 MPa | - | - | - | Predicted Value, RP002 |