ASTM A519 Grade 1137 Cold Worked
Equivalent material: DIN 1.0764, DIN 36SMn14, AFNOR 36SMn14, BS 36SMn14, BS 216M36, AISI 1137, SAE 1137, JIS SUM41, EN 36SMn14, EN 1.0764, ISO 36SMn14, ASTM Grade 1137, UNS G11370, DIN 1.0765, DIN 35MF6Pb14, AFNOR 35MF6Pb14, BS 35MF6Pb14, AISI 11L37, SAE 11L37, EN 36SMnPb14, EN 1.0765, ISO 35MF6Pb14, GOST AS35G2
ASTM A519 Grade 1137 Cold Worked general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Manganese Steel |
ASTM A519 Grade 1137 Cold Worked thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.33E-5 1/K |
Typical for Manganese Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Manganese Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 510 - 553 J/(kg·K) |
Typical for Manganese Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 16 W/(m·K) |
Typical for Manganese Steel |
ASTM A519 Grade 1137 Cold Worked chemical
| Property |
Value |
| Carbon |
Carbon of 0.32 - 0.39 % |
| Manganese |
Manganese of 1.35 - 1.65 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Sulfur |
Sulfur of 0.08 - 0.13 % |
ASTM A519 Grade 1137 Cold Worked mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Manganese Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 5 % |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 85 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Manganese Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 550 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 450 MPa |
- |