ASTM A513 Grade 1340 As-Welded
Equivalent material: AISI 1340, SAE 1340, UNS G13400
ASTM A513 Grade 1340 As-Welded general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Manganese Steel |
ASTM A513 Grade 1340 As-Welded thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.33E-5 1/K |
Typical for Manganese Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Manganese Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 510 - 553 J/(kg·K) |
Typical for Manganese Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 16 W/(m·K) |
Typical for Manganese Steel |
ASTM A513 Grade 1340 As-Welded chemical
| Property |
Value |
| Carbon |
Carbon of 0.38 - 0.43 % |
| Manganese |
Manganese of 1.6 - 1.9 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.04 % |
ASTM A513 Grade 1340 As-Welded mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Manganese Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 10 % |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 80 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Manganese Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 495 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 380 MPa |
- |