ASTM A487 Grade CA6NM Class B, Heat-Treated
Equivalent material: DIN 1.4313, DIN G-X5CrNi13-4, DIN X4CrNi13-4, AFNOR Z6CN13-04, BS 425C11, AISI 415, AISI S41500, SAE 415, SAE S41500, JIS SUSF6NM, JIS SCS5, JIS SCS6, EN X3CrNiMo13-4, EN GX5CrNi134, EN 1.4313, ASTM CA6NM, ASTM F6NM, UNS J91540, UNS S41500, UNS S42400, ASTM CA6NM-A
ASTM A487 Grade CA6NM Class B, Heat-Treated general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
ASTM A487 Grade CA6NM Class B, Heat-Treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
ASTM A487 Grade CA6NM Class B, Heat-Treated chemical
| Property |
Value |
| Carbon |
Carbon of 0.06 % |
| Copper |
Copper of 0.1 % |
| Manganese |
Manganese of 1 % |
| Molybdenum |
Molybdenum of 0.4 - 1 % |
| Nickel |
Nickel of 0.05 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A487 Grade CA6NM Class B, Heat-Treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
ASTM A487 Grade CA6NM Class B, Heat-Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A50 |
20.0 °C |
Elongation A50 of 17 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 255 [-] |
- |
| Hardness, Rockwell C |
20.0 °C |
Hardness, Rockwell C of 23 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 35 % |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 690 MPa |
- |
| Yield Strength Rp0.2, short transverse |
20.0 °C |
Yield Strength Rp0.2, short transverse of 515 MPa |
- |