ASTM A463 SS Grade 230 Aluminum-Coated by the Hot-Dip Process
Equivalent material: DIN 1.0242, DIN StE 250-2 Z, DIN S250GD, AFNOR S250GD, BS S250GD, JIS SGC340, JIS SGMC340, JIS SGMH340, JIS SZAC340, JIS SZAH340, EN S250GD, EN 1.0242, ISO 250, GOST 250, GB/T S250GD
ASTM A463 SS Grade 230 Aluminum-Coated by the Hot-Dip Process general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A463 SS Grade 230 Aluminum-Coated by the Hot-Dip Process thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A463 SS Grade 230 Aluminum-Coated by the Hot-Dip Process chemical
| Property |
Value |
| Carbon |
Carbon of 0.2 % |
| Chromium |
Chromium of 0.15 % |
| Copper |
Copper of 0.2 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 0.2 % |
| Niobium |
Niobium of 8E-3 % |
| Phosphorus |
Phosphorus of 0.4 % |
| Sulfur |
Sulfur of 0.04 % |
| Titanium |
Titanium of 0.3 % |
| Vanadium |
Vanadium of 8E-3 % |
ASTM A463 SS Grade 230 Aluminum-Coated by the Hot-Dip Process magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A463 SS Grade 230 Aluminum-Coated by the Hot-Dip Process electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A463 SS Grade 230 Aluminum-Coated by the Hot-Dip Process mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 20 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 310 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 230 MPa |
- |
Our steel products inspire endless possibilities while ensuring engineering excellence.
-- Our promise
Similar or equivalent steel materials