ASTM A463 Grade FSS Type 439 Aluminum-Coated by the Hot-Dip Process
ASTM A463 Grade FSS Type 439 Aluminum-Coated by the Hot-Dip Process general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.6 - 7.8 g/cm³ | Typical for Ferritic Stainless Steel |
ASTM A463 Grade FSS Type 439 Aluminum-Coated by the Hot-Dip Process thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K | Typical for Ferritic Stainless Steel |
| Melting point | - | Melting point of 1425 - 1530 °C | Typical for Ferritic Stainless Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 420 - 586 J/(kg·K) | Typical for Ferritic Stainless Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 11 - 22 W/(m·K) | Typical for Ferritic Stainless Steel |
ASTM A463 Grade FSS Type 439 Aluminum-Coated by the Hot-Dip Process chemical
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.15 % |
| Carbon | Carbon of 0.03 % |
| Chromium | Chromium of 17 - 19 % |
| Copper | Copper of 0.5 % |
| Manganese | Manganese of 1 % |
| Molybdenum | Molybdenum of 0.06 % |
| Nickel | Nickel of 0.5 % |
| Phosphorus | Phosphorus of 0.04 % |
| Sulfur | Sulfur of 0.03 % |
ASTM A463 Grade FSS Type 439 Aluminum-Coated by the Hot-Dip Process electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 6E-7 - 7.5E-7 Ω·m | Typical for Ferritic Stainless Steel |
ASTM A463 Grade FSS Type 439 Aluminum-Coated by the Hot-Dip Process mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 220 GPa | Typical for Ferritic Stainless Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 22 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Ferritic Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Ferritic Stainless Steel |
| Yield strength | 23.0 °C | Yield strength of 205 - 415 MPa | - |