ASTM A426 Grade CP22 Austenitized and Tempered
Equivalent material: DIN 1.7379, DIN G17CrMo9-10, DIN GS-18CrMo9-10, EN GS-18CrMo9-10, EN G17CrMo9-10, EN 1.7379, ASTM CP22, UNS J21890, DIN 1.7387, DIN G12CrMo9-10, JIS SCPH32, EN 1.7387
ASTM A426 Grade CP22 Austenitized and Tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Molybdenum Steel |
ASTM A426 Grade CP22 Austenitized and Tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K |
Typical for Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 502 J/(kg·K) |
Typical for Chromium Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 - 43 W/(m·K) |
Typical for Chromium Molybdenum Steel |
ASTM A426 Grade CP22 Austenitized and Tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.05 - 0.15 % |
| Chromium |
Chromium of 2 - 2.75 % |
| Manganese |
Manganese of 0.3 - 0.7 % |
| Molybdenum |
Molybdenum of 0.9 - 1.2 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.025 % |
ASTM A426 Grade CP22 Austenitized and Tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Molybdenum Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 20 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 201 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 35 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 485 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 275 MPa |
- |