ASTM A36
ASTM A36 general
| Property | Value | Comment |
|---|---|---|
| Density | Density of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
ASTM A36 thermal
| Property | Value | Comment |
|---|---|---|
| Coefficient of thermal expansion | Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K | Typical for Low Carbon Steel |
| Max service temperature | Max service temperature of 341.1 °C | Predicted Value, Long |
| - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | Specific heat capacity of 465 J/(kg·K) | Typical for Low Carbon Steel |
| Thermal conductivity | Thermal conductivity of 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
ASTM A36 chemical
| Property | Value | Related Standards | Shape |
|---|---|---|---|
| Carbon | Carbon of 0.26 % | ASTM A36 | Plate, Bar |
| Copper | Copper of 0.2 % | ASTM A36 | Plate, Bar |
| Phosphorus | Phosphorus of 0.04 % | ASTM A36 | Plate, Bar |
| Silicon | Silicon of 0.4 % | ASTM A36 | Plate, Bar |
| Sulfur | Sulfur of 0.05 % | ASTM A36 | Plate, Bar |
ASTM A36 magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
ASTM A36 electrical
| Property | Value | Comment |
|---|---|---|
| Electrical conductivity | Electrical conductivity of 8 S/m | Predicted Value |
| Electrical resistivity | Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m | Typical for Carbon Steel |
ASTM A36 mechanical
| Property | Value | Related Standards | Shape | Comment |
|---|---|---|---|---|
| Elastic modulus | Elastic modulus of 200 - 215 GPa | - | - | Typical for Low Carbon Steel |
| Elongation | Elongation of 18.6 % | - | - | Predicted Value, A80 |
| - | Elongation of 18.7 % | - | - | Predicted Value, Transverse |
| - | Elongation of 19.5 % | - | - | Predicted Value, A80 Transverse |
| - | Elongation of 20 % | ASTM A36 | Plate, Bar | A200 |
| - | Elongation of 21 % | ASTM A36 | - | A50 |
| - | Elongation of 23 % | ASTM A36 | Plate, Bar | A50 |
| - | Elongation of 24.8 % | - | - | Predicted Value |
| Poisson's ratio | Poisson's ratio of 0.29 [-] | - | - | Typical for Low Carbon Steel |
| Reduction of area | Reduction of area of 43.6 % | - | - | Predicted Value, Transverse |
| - | Reduction of area of 44.0 % | - | - | Predicted Value |
| Shear modulus | Shear modulus of 82 GPa | - | - | Typical for Low Carbon Steel |
| Shear strength | Shear strength of 560.7 MPa | - | - | Predicted Value |
| Tensile strength | Tensile strength of 400 - 550 MPa | ASTM A36 | Plate, Bar | - |
| Yield strength | Yield strength of 250 MPa | ASTM A36 | Plate, Bar | - |
| - | Yield strength of 266.7 MPa | - | - | Predicted Value, RP05 |
| - | Yield strength of 278.4 MPa | - | - | Predicted Value, RP1 |
| - | Yield strength of 303.5 MPa | - | - | Predicted Value, Transverse |
| - | Yield strength of 316.1 MPa | - | - | Predicted Value, RP1 Transverse |
| - | Yield strength of 324.8 MPa | - | - | Predicted Value, RP02 |
| - | Yield strength of 441.6 MPa | - | - | Predicted Value, RP002 |
| - | Yield strength of 496.5 MPa | - | - | Predicted Value, RP02 Transverse |