ASTM A353 Double-Normalized and Tempered
ASTM A353 Double-Normalized and Tempered general
| Property | Value | Comment |
|---|---|---|
| Density | Density of 8.8 g/cm³ | Typical for Nickel Steel |
ASTM A353 Double-Normalized and Tempered thermal
| Property | Value | Comment |
|---|---|---|
| Coefficient of thermal expansion | Coefficient of thermal expansion of 12.25 1/K | Predicted Value |
| Melting point | Melting point of 1316 - 1595 °C | Typical for Nickel Steel |
| Specific heat capacity | Specific heat capacity of 456 J/(kg·K) | Typical for Nickel Steel |
| Thermal conductivity | Thermal conductivity of 10 - 50 W/(m·K) | Typical for Nickel Steel |
ASTM A353 Double-Normalized and Tempered chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Carbon | Carbon of 0.13 % | Double-Normalized and Tempered | ASTM A353 | Plate |
| Manganese | Manganese of 0.9 % | Double-Normalized and Tempered | ASTM A353 | Plate |
| Nickel | Nickel of 8.5 - 9.5 % | Double-Normalized and Tempered | ASTM A353 | Plate |
| Phosphorus | Phosphorus of 0.015 % | Double-Normalized and Tempered | ASTM A353 | Plate |
| Silicon | Silicon of 0.15 - 0.4 % | Double-Normalized and Tempered | ASTM A353 | Plate |
| Sulfur | Sulfur of 0.015 % | Double-Normalized and Tempered | ASTM A353 | Plate |
ASTM A353 Double-Normalized and Tempered electrical
| Property | Value | Comment |
|---|---|---|
| Electrical conductivity | Electrical conductivity of 7 S/m | Predicted Value |
| Electrical resistivity | Electrical resistivity of 35 Ω·m | Predicted Value |
ASTM A353 Double-Normalized and Tempered mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
| Elastic modulus | Elastic modulus of 200 - 215 GPa | - | - | - | Typical for Nickel Steel |
| Elongation | Elongation of 16.4 % | - | - | - | Predicted Value, A200 |
| - | Elongation of 18.4 % | - | - | - | Predicted Value, Transverse |
| - | Elongation of 20 % | Double-Normalized and Tempered | ASTM A353 | Plate | A50 |
| - | Elongation of 21.1 % | - | - | - | Predicted Value |
| - | Elongation of 22.2 % | - | - | - | Predicted Value, A80 |
| - | Elongation of 29.0 % | - | - | - | Predicted Value, A80 Transverse |
| Poisson's ratio | Poisson's ratio of 0.291 [-] | - | - | - | Typical for Nickel Steel |
| Reduction of area | Reduction of area of 42.6 % | - | - | - | Predicted Value, Transverse |
| - | Reduction of area of 44.7 % | - | - | - | Predicted Value |
| Shear modulus | Shear modulus of 76 GPa | - | - | - | Typical for Nickel Steel |
| Shear strength | Shear strength of 581.2 MPa | - | - | - | Predicted Value |
| Tensile strength | Tensile strength of 690 - 825 MPa | Double-Normalized and Tempered | ASTM A353 | Plate | - |