ASTM A336 Grade F6NM Annealed or Normalized and Tempered
Equivalent material: DIN 1.4313, DIN G-X5CrNi13-4, DIN X4CrNi13-4, AFNOR Z6CN13-04, BS 425C11, AISI 415, AISI S41500, SAE 415, SAE S41500, JIS SUSF6NM, JIS SCS5, JIS SCS6, EN X3CrNiMo13-4, EN GX5CrNi134, EN 1.4313, ASTM CA6NM, UNS J91540, UNS S41500, UNS S42400
ASTM A336 Grade F6NM Annealed or Normalized and Tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
ASTM A336 Grade F6NM Annealed or Normalized and Tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
ASTM A336 Grade F6NM Annealed or Normalized and Tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.05 % |
| Chromium |
Chromium of 11.5 - 14 % |
| Manganese |
Manganese of 0.5 - 1 % |
| Molybdenum |
Molybdenum of 0.5 - 1 % |
| Nickel |
Nickel of 3.5 - 5.5 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.015 % |
ASTM A336 Grade F6NM Annealed or Normalized and Tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
ASTM A336 Grade F6NM Annealed or Normalized and Tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 15 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 45 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 790 - 965 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 620 MPa |
- |