ASTM A320 Grade B8C Class 1, Carbide Solution Treated
Equivalent material: AISI 347, SAE 347, JIS SUS347, ASTM TP347, ASTM 347, ASTM S34700, ASTM Grade F347, ASTM Grade B8C, ASTM Grade B8CA, UNS S34700
ASTM A320 Grade B8C Class 1, Carbide Solution Treated general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
ASTM A320 Grade B8C Class 1, Carbide Solution Treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
ASTM A320 Grade B8C Class 1, Carbide Solution Treated chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 % |
| Chromium |
Chromium of 17 - 19 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 9 - 12 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A320 Grade B8C Class 1, Carbide Solution Treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
ASTM A320 Grade B8C Class 1, Carbide Solution Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A50 |
20.0 °C |
Elongation A50 of 30 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 223 [-] |
- |
| Hardness, Rockwell B |
20.0 °C |
Hardness, Rockwell B of 96 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 50 % |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 515 MPa |
- |
| Yield Strength Rp0.2, short transverse |
20.0 °C |
Yield Strength Rp0.2, short transverse of 205 MPa |
- |