ASTM A276 Grade S20162 Annealed; Hot-Finished or Cold finished
Equivalent material: UNS S20162
ASTM A276 Grade S20162 Annealed; Hot-Finished or Cold finished general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.9 - 8.2 g/cm³ | Typical for Austenitic Stainless Steel |
ASTM A276 Grade S20162 Annealed; Hot-Finished or Cold finished thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K | Typical for Austenitic Stainless Steel |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 440 J/(kg·K) | Typical for Austenitic Stainless Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 11 - 21 W/(m·K) | Typical for Austenitic Stainless Steel |
ASTM A276 Grade S20162 Annealed; Hot-Finished or Cold finished chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.15 % |
| Chromium | Chromium of 16.5 - 21 % |
| Manganese | Manganese of 4 - 8 % |
| Molybdenum | Molybdenum of 0.5 - 2.5 % |
| Nickel | Nickel of 6 - 10 % |
| Nitrogen | Nitrogen of 0.05 - 0.25 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 2.5 - 4.5 % |
| Sulfur | Sulfur of 0.04 % |
ASTM A276 Grade S20162 Annealed; Hot-Finished or Cold finished electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
ASTM A276 Grade S20162 Annealed; Hot-Finished or Cold finished mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 195 GPa | Typical for Austenitic Stainless Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 50 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
| Reduction of area | 23.0 °C | Reduction of area of 60 % | - |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
| Tensile strength | 23.0 °C | Tensile strength of 690 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 345 MPa | - |